PolyOne Stat-Tech™ AS-08CF/000 UV FR V0 Acrylonitrile Butadiene Styrene (ABS)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | PolyOne Corporation |
| Trade Name | Stat-Tech™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Stat-Tech™ AS-08CF/000 UV FR V0 Acrylonitrile Butadiene Styrene (ABS).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compounds combine the performance of select engineering resins with reinforcing additives such as carbon powder, carbon fiber, nickel-coated carbon fiber and stainless steel fiber, for low-to-high levels of conductivity depending upon application requirements.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 65.5 MPa | 9500 psi | Type I, 5.1 mm/min; ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 4.83 GPa | 701 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 4.69 GPa | 680 ksi | ASTM D790 |
| Izod Impact, Notched | 0.430 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
0.806 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
BK; Internal Method |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+6 ohm-cm | 1.00e+6 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+7 ohm | 1.00e+7 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 221 - 249 °C | 430 - 480 °F | |
| Mold Temperature | 26.7 - 54.4 °C | 80.1 - 130 °F | |
| Drying Temperature | 76.7 °C | 170 °F | |
| Dry Time | 2.00 hour | 2.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Antistatic | |
| Electromagnetic Shielding (EMI) | ||
| ESD Protection | ||
| Radio Frequency Shielding (RFI) | ||
| Filler / Reinforcement | Carbon Fiber Reinforcement, 8.0% Filler by Weight | |
| Forms | Pellets | |
| Generic Material | ABS | |
| Generic Name | Acrylonitrile Butadiene Styrene (ABS) | |
| Processing Method | Injection Molding | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| RoHS Compliance | RoHS Compliant | |
| Uses | Aerospace Applications | |
| Automotive Under the Hood | ||
| Business Equipment | ||
| Electrical/Electronic Applications | ||
| Housings | ||
| Printer Parts |
Users viewing this material also viewed the following:
- Karina E TR-600D48/1 Black PVC Compound
- LyondellBasell Alathon® H6012 High Density Polyethylene, MMW Film Grade
- Multibase Multi-Flex® A 0740 TPE Thermoplastic Elastomer
- SABIC Innovative Plastics LNP THERMOCOMP ZF406XXX PPO Blend (Asia Pacific)
- Arlon T3020-B002-## 0.020" Self-Fusing, Cured Silicone Rubber Tape with Fiberglass Substrate
- A. Schulman ComAlloy Hiloy® 132 Polypropylene, Glass/Mineral Reinforced, Chemically Coupled
- Aleris HOGAL 5558 Aluminum 5026 H14/H34
- Owens Corning Glass Fiber Reinforced Polyester, Woven Roving (Lay-up), 50 wt.% glass
Copyright © lookpolymers.com All Rights Reserved