PolyOne LubriOne™ NY-10GF/10T BLACK Polyamide 6 (Nylon 6)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | PolyOne Corporation |
| Trade Name | LubriOne™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne LubriOne™ NY-10GF/10T BLACK Polyamide 6 (Nylon 6).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Water Absorption | 1.4 % | 1.4 % | @ 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 117 | 117 | ASTM D785 |
| Tensile Strength at Break | 93.1 MPa | 13500 psi | Type I, 5.1 mm/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 4.65 GPa | 674 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 117 MPa | 17000 psi | ASTM D790 |
| Flexural Modulus | 3.93 GPa | 570 ksi | ASTM D790 |
| Compressive Strength | 96.5 MPa | 14000 psi | ASTM D695 |
| Izod Impact, Notched | 0.800 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.50 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C @Thickness 3.18 mm |
390 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 182 °C @Thickness 3.18 mm |
360 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| Flammability, UL94 | HB | HB | UL 94 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 232 - 260 °C | 450 - 500 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 79.4 - 93.3 °C | 175 - 200 °F | |
| Dry Time | 2.00 hour | 2.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Filler / Reinforcement | Glass Fiber Reinforcement | |
| Forms | Pellets | |
| Generic Material | Nylon 6 | |
| Generic Name | Polyamide 6 (Nylon 6) | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® HFD1212 PC Copolymer (Asia Pacific)
- Kuraray HYBRAR® PP1 Thermoplastic Rubber-Polypropylene Blend
- SABIC Innovative Plastics LNP LUBRICOMP EL003 PEI (Asia Pacific)
- Teknor Apex APEX® 157-V Polyvinyl Chloride, Flexible
- Sumitomo Bakelite North America 52-01 Short-Glass Reinforced Diallyl Phthalate
- SABIC Innovative Plastics LNP THERMOCOMP RC003SXS PA 66 (Europe-Africa-Middle East)
- A. Schulman PP 1667-01 Polypropylene Natural Homopolymer Polypropylene
- ConocoPhillips Conoflex® 32 SRI Lubricant ISO
Copyright © lookpolymers.com All Rights Reserved