- PolyOne Lubri-Tech™ PK-30CF/15T Polyetheretherketone (PEEK), Carbon Fiber Reinforced, PTFE Lubricated (discon
PolyOne Lubri-Tech™ PK-30CF/15T Polyetheretherketone (PEEK), Carbon Fiber Reinforced, PTFE Lubricated (discon
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ PK-30CF/15T Polyetheretherketone (PEEK), Carbon Fiber Reinforced, PTFE Lubricated
(discon.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Carbon Fiber ReinforcedPTFE LubricatedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.532 g/cc | 1.532 g/cc | ASTM D792 |
| Water Absorption | 0.080 % @Thickness 3.17 mm |
0.080 % @Thickness 0.125 in |
24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 183 MPa | 26500 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 13.8 GPa | 2000 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 262 MPa | 38000 psi | ASTM D790 |
| Flexural Modulus | 13.8 GPa | 2000 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
2.00 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 299 °C | 570 °F | Unannealed, 0.250 in bars; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 10 - 100 ohm-cm | 10 - 100 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 10 - 100 ohm | 10 - 100 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 399 - 427 °C | 750 - 800 °F | Molding |
| Mold Temperature | >= 149 °C | >= 300 °F | |
| Drying Temperature | 149 °C | 300 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Polykemi AB SCANMID 6 B32^ E Q30 Nylon 6, Glass Fiber Reinforced, Modified
- PolyOne Elastamax™ XL-2060 Black 2001 Thermoplastic Polyolefin Elastomer (TPO (POE))
- Freudenberg Simrit V177 Fluoroelastomer Self-Lube
- Momentive Performance Materials Siloprenâ„¢ LSR 3785/30 Liquid Silicone Rubber - Self-Lubricating / Standard
- Saint-Gobain T-Bond II® Semi-Rigid Polyurethane Foam Structural Glazing and Cladding Spacer System
- Arkema Group OREVAC® 18921A Epoxide Modified Polyethylene
- AK Steel Cold Rolled Carbon Steel, Bake Hardenable (BH 180), SAE J2340 Type 180 B
- Arkema Group Orgalloy® P 60AD Nylon (Conditioned)
Copyright © lookpolymers.com All Rights Reserved