PolyOne Lubri-Tech™ PK-000/15T Polyetheretherketone - 15% PTFE Lubricated (discontinued **)
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, PTFE-Filled |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ PK-000/15T Polyetheretherketone - 15% PTFE Lubricated
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by PolyOne.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0060 - 0.0080 cm/cm @Thickness 3.17 mm |
0.0060 - 0.0080 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 90.0 MPa | 13100 psi | ASTM D638 |
| Elongation at Break | 1.0 - 3.0 % | 1.0 - 3.0 % | ASTM D638 |
| Tensile Modulus | 4.50 GPa | 653 ksi | ASTM D638 |
| Flexural Yield Strength | 103 MPa | 14900 psi | ASTM D790 |
| Flexural Modulus | 4.50 GPa | 653 ksi | ASTM D790 |
| Izod Impact, Notched | 0.530 - 0.690 J/cm @Thickness 6.35 mm |
0.993 - 1.29 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 371 - 399 °C | 700 - 750 °F | Stock |
| Mold Temperature | 149 °C | 300 °F | |
| Drying Temperature | 149 °C | 300 °F |
Users viewing this material also viewed the following:
- Parker Chomerics WIN-SHIELD™ C (Cast Allycarbonate) EMI Shielded Window
- Indium Corp. Indalloy® 97 Pb-Sn-Bi Solder Alloy
- A. Schulman SCHULADUR® A GF10 10% Glass Fiber Reinforced PBT
- Chevron Phillips Marlex® 1009 LDPE Injection Molding Resin
- ExxonMobil Escorene™ UL 00018 Ethylene Vinyl Acetate Copolymer (European Grade)
- Braskem Green PE SLL218 Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene
- Barlog Plastics KEBAFLEX E 65.1 TPE-V, Shore A65
- AK Steel Cold Rolled Carbon Steel, Bake Hardenable (BH 180), SAE J2340 Type 180 B
Copyright © lookpolymers.com All Rights Reserved