- PolyOne Lubri-Tech™ NI-30GF/15T Nylon 6/10 - 30% Glass Fiber Reinforced - 15% PTFE Lubricated (discontinued *
PolyOne Lubri-Tech™ NI-30GF/15T Nylon 6/10 - 30% Glass Fiber Reinforced - 15% PTFE Lubricated (discontinued *
| Category | Polymer , Thermoplastic , Nylon , Nylon 610 , Nylon 610, Glass Reinforced |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ NI-30GF/15T Nylon 6/10 - 30% Glass Fiber Reinforced - 15% PTFE Lubricated
(discontinued *.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by PolyOne.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm @Thickness 3.17 mm |
0.0030 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 131 MPa | 19000 psi | ASTM D638 |
| Elongation at Break | 3.0 - 4.0 % | 3.0 - 4.0 % | ASTM D638 |
| Tensile Modulus | 6.90 GPa | 1000 ksi | ASTM D638 |
| Flexural Yield Strength | 207 MPa | 30000 psi | ASTM D790 |
| Flexural Modulus | 6.90 GPa | 1000 ksi | ASTM D790 |
| Izod Impact, Notched | 1.87 J/cm @Thickness 6.35 mm |
3.50 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 48.6 µm/m-°C @Temperature 20.0 °C |
27.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 288 °C | 500 - 550 °F | Stock |
| Mold Temperature | 93.0 °C | 199 °F | |
| Drying Temperature | 77.0 °C | 171 °F |
Users viewing this material also viewed the following:
- Polycasa LENTICULAR PETG
- DuPont Performance Polymers Delrin® FG500P NC010 Acetal Homopolymer (Unverified Data**)
- North Wood Plastics PS with 40% Wood Fiber
- Industrial Laminates/Norplex NP630 Paper Base Laminate
- Karina E 854-35/9-A-ERYB Ivory PVC Compound
- Teknor Apex APEX® 3701-60NT Polyvinyl Chloride, Flexible
- Total PPC 4524WZ Polypropylene, Impact Copolymer
- BASF Palatinol® N Diisononyl Phthalate
Copyright © lookpolymers.com All Rights Reserved