PolyOne Lubri-Tech™ ATH-000/5M Acetal-Homopolymer (discontinued **)
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ ATH-000/5M Acetal-Homopolymer
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Molybdenum Disulfide LubricatedInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 |
| Water Absorption | 0.050 % @Thickness 3.17 mm |
0.050 % @Thickness 0.125 in |
24 hr immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.020 - 0.025 cm/cm | 0.020 - 0.025 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 34.5 MPa | 5000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 2.55 GPa | 370 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 34.5 MPa | 5000 psi | ASTM D790 |
| Flexural Modulus | 2.55 GPa | 370 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.50 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 260 °F | Unannealed, 0.125 in bars; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 121 °C | 250 °F | Unannealed, 0.125 in bars; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® HPS1 PC (Europe-Africa-Middle East)
- KKPC KOSYN KSL 208 Styrene-Butadiene Latex
- Lucas-Milhaupt Lucanex 616 Active Metal Brazing
- Momentive Performance Materials Siloprenâ„¢ LSR 2030 Liquid Silicone Rubber - General Purpose
- SABIC Innovative Plastics NORYL GTX GTX975 PPE+PA (Asia Pacific)
- SABIC Innovative Plastics NORYL NH8006 PPE+HIPS
- Wellman Wellamid® FRGFT1741-BK2 Nylon 66, 32% Glass Fiber Reinforced, Flame Retardant
- Total PPC 3660 Polypropylene, Heterophasic Copolymer
- A. Schulman POLYFORT™ FPP 1080 Glass Fiber-Reinforced Homopolymer Polypropylene
- KKPC KOSYN KTR 601 Thermoplastic Elastomer (TPE)
Copyright © lookpolymers.com All Rights Reserved