- PolyOne Geon™ Vinyl Rigid Molding M4825 Polyvinyl Chloride, Rigid (PVC, Rigid)
PolyOne Geon™ Vinyl Rigid Molding M4825 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Rigid Molding M4825 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
** NOTE: UL REGULATORY LISTING PENDINGInformation provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | ASTM D955 |
| Spiral Flow | 109.22 cm | 43.000 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 84 | 84 | ASTM D2240 |
| Tensile Strength, Yield | 62.7 MPa | 9090 psi | Type I, 51 mm/min; ASTM D638 |
| Elongation at Break | 16 % | 16 % | Type I, 51 mm/min; ASTM D638 |
| Tensile Modulus | 3.29 GPa | 477 ksi | Type I, 51 mm/min; ASTM D638 |
| Flexural Strength | 96.5 MPa | 14000 psi | ASTM D790 |
| Flexural Modulus | 3.24 GPa | 470 ksi | ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
0.993 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 63.9 °C @Thickness 6.35 mm |
147 °F @Thickness 0.250 in |
Annealed; ASTM D648 |
| 66.1 °C @Thickness 6.35 mm |
151 °F @Thickness 0.250 in |
Unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C @Thickness 6.35 mm |
140 °F @Thickness 0.250 in |
Annealed; ASTM D648 |
| 63.0 °C @Thickness 6.35 mm |
145 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 4.0 % @Thickness 3.81 mm |
4.0 % @Thickness 0.150 in |
ASTM D1003 |
| Transmission, Visible | 75 % @Thickness 3.81 mm |
75 % @Thickness 0.150 in |
ASTM D1003 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 199 - 204 °C | 390 - 399 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Clear/Transparent | |
| Features | General Purpose | |
| High Flow | ||
| Forms | Pellets | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Product Description | ** NOTE: UL REGULATORY LISTING PENDING | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | General Purpose |
Users viewing this material also viewed the following:
- Omni Plastics OmniLon™ 6 PA6 GR40 NA Glass Reinforced Nylon
- Pyrotek TS-105 Thermoset Electrical Insulation Product (Nema Grade: G-5)
- SABIC Innovative Plastics Lexan® 915R PC
- Unifrax Foamfrax® HD Grade II Fiber HD Insulation
- Covestro Makrolon® FU1007 Polycarbonate
- Azoty Tarnow™ Tarnamid® T-27 TF10 Polyamide 6 - Improved Slip Properties
- Adamas Adalon® 508 PTFE, 1% MoS2
- A. Schulman POLYFORT™ FPP 1068-32 Black40% Mineral Filled Polypropylene
Copyright © lookpolymers.com All Rights Reserved