PolyOne Geon™ Vinyl Rigid Extrusion L9630 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Rigid Extrusion L9630 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product can meet UL-94V-0. Material passed V-0 @ 1.5mm in screening test at PDI.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 82 | 82 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 43.1 MPa | 6250 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 3.12 GPa | 453 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 73.8 MPa | 10700 psi | ASTM D790 |
| Flexural Modulus | 2.92 GPa | 424 ksi | ASTM D790 |
| Izod Impact, Notched | 2.30 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
4.31 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Flow; ASTM D256A |
| 3.00 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
5.62 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Across Flow; ASTM D256A | |
| 9.00 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
16.9 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A | |
| Dart Drop Total Energy | 62.7 J/cm @Temperature 23.0 °C |
0.117 ft-lb/mil @Temperature 73.4 °F |
Procedure A, C.125; ASTM D4226 |
| 165 J/cm @Temperature 23.0 °C |
0.309 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 67.0 µm/m-°C | 37.2 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 72.5 °C @Thickness 3.18 mm |
163 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 182 - 193 °C | 360 - 379 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ease of Sizing | Acceptable | |
| Features | Good Surface Finish | |
| Forms | Pellets | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Processing Method | Extrusion | |
| PVC Cell Classification | 16354 | ASTM D1784 |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Edge Banding | |
| Profiles |
Users viewing this material also viewed the following:
- REXtac Rextac® RT 2330 Amorphous Polyalphaolefin (APAO)
- OCTAL DPET™/PE Laminate Sheet with Improved Barrier Properties
- Polymer Resources PC-UV2-D-[color]-1 Polycarbonate, UV-stabilized, Medium Flow with Mold Release
- Lehmann & Voss LUVOCOM® 80-8162 Polyacetal-copolymer, lubricant modified
- Magyar Aluminum ALO-P90-02 Alumina
- LG Chemical LUPOY SR3108L PC, High Impact
- KKPC KOSYN KBR 710S Polybutadiene Rubber (Low cis BR)
- Shandong Dongyue Polymer DF-31A PTFE Pelletized Resin
- ExxonMobil Bicor™ 25MB400 OPP Film
- Aremco AREMCOLOX™ 502-1400 (Full-Fired) Dense Alumina
Copyright © lookpolymers.com All Rights Reserved