PolyOne Geon™ Vinyl Rigid Extrusion 87570 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Rigid Extrusion 87570 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 83 | 83 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 42.2 MPa | 6120 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 3.36 GPa | 487 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 77.2 MPa | 11200 psi | ASTM D790 |
| Flexural Modulus | 3.19 GPa | 463 ksi | ASTM D790 |
| Izod Impact, Notched | 0.690 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
1.29 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Flow; ASTM D256A |
| 3.80 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
7.12 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A | |
| 8.50 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
15.9 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Across Flow; ASTM D256A | |
| Dart Drop Total Energy | 46.7 J/cm @Temperature 23.0 °C |
0.0875 ft-lb/mil @Temperature 73.4 °F |
Procedure A, C.125; ASTM D4226 |
| 46.7 J/cm @Temperature 23.0 °C |
0.0875 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 62.0 µm/m-°C | 34.4 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.0 °C @Thickness 3.18 mm |
160 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 182 - 193 °C | 360 - 379 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Agency Ratings | ASTM E 84 | |
| Appearance | Translucent | |
| Features | Low Smoke Emission | |
| Forms | Pellets | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Processing Method | Extrusion | |
| PVC Cell Classification | 14344 | ASTM D1784 |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Profiles |
Users viewing this material also viewed the following:
- Precision Polymer Engineering S75T Silicone Rubber
- Haynes Hastelloy® C-22HS™ Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform
- Teknor Apex APEX® 90-A472R-100-NT Polyvinyl Chloride, Flexible
- Wico Plast Wicolon 407 Polycarbonate, U.V. Stabilized
- EMS-Griltech Griltex® 6E Copolyester Hotmelt Adhesive (Technical Applications)
- Adamas Adalon® 704 PTFE, Long Carbon Fiber
- Asahi Kasei Xyron® 300V Modified Polyphenylene Ether
- PolyOne Edgetek® PI-40CF/000 Polyetherimide (PEI), Carbon Fiber Reinforced (discontinued **)
Copyright © lookpolymers.com All Rights Reserved