PolyOne Geon™ L4605 Red 7640 Polyvinyl Chloride, Semi-Rigid (PVC, Semi-Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ L4605 Red 7640 Polyvinyl Chloride, Semi-Rigid (PVC, Semi-Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 74 | 74 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 23.8 MPa | 3450 psi | 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 1.82 GPa | 264 ksi | 5.1 mm/min; ASTM D638 |
| Flexural Yield Strength | 50.7 MPa | 7350 psi | 13 mm/min; ASTM D790 |
| Flexural Modulus | 1.73 GPa | 251 ksi | 13 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.400 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
0.749 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded; ASTM D256 |
| Dart Drop Total Energy | 70.3 J/cm @Temperature 23.0 °C |
0.132 ft-lb/mil @Temperature 73.4 °F |
extruded profile, Procedure A, C.125; ASTM D4226 |
| 72.1 J/cm @Temperature 23.0 °C |
0.135 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 73.0 µm/m-°C | 40.6 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 41.1 °C @Thickness 3.18 mm |
106 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| 43.9 °C @Thickness 3.18 mm |
111 °F @Thickness 0.125 in |
Annealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 36.1 °C @Thickness 3.18 mm |
97.0 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| 36.1 °C @Thickness 3.18 mm |
97.0 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 5.0 - 30 % | 5.0 - 30 % | 60°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 182 - 193 °C | 360 - 379 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Medium Gloss | |
| Forms | Pellets | |
| Generic Material | PVC, Semi-Rigid | |
| Generic Name | Polyvinyl Chloride, Semi-Rigid (PVC, Semi-Rigid) | |
| Processing Method | Coextrusion | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Capstock | |
| Outdoor Applications |
Users viewing this material also viewed the following:
- Petromont 1201 High Density Polyethylene Resin
- SABIC Innovative Plastics LNP LUBRICOMP DFI14 PC
- Huntsman AVALON® 90 AB Thermoplastic Polyurethane
- Karina E 57/201-D-IS-SD Compound PVC Crystal
- Schwartz Technical Plastics LAMIGAMID® 320 Cast Polyamide 6, Conditioned
- SABIC Innovative Plastics Valox® V3802 PBT + PC + PET (Asia Pacific)
- ExxonMobil Enable™ 20-10CB Metallocene Polyethylene Resin (European Grade)
- ExxonMobil HDPE HD 7960..13 High Density Polyethylene Resin
- E-Polymers TEKASTER® F101M Unreinforced impact modified PBT
Copyright © lookpolymers.com All Rights Reserved