PolyOne Geon™ L4605 Ivory 3098 Polyvinyl Chloride, Semi-Rigid (PVC, Semi-Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ L4605 Ivory 3098 Polyvinyl Chloride, Semi-Rigid (PVC, Semi-Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 76 | 76 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 30.4 MPa | 4410 psi | 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.01 GPa | 292 ksi | 5.1 mm/min; ASTM D638 |
| Flexural Yield Strength | 54.1 MPa | 7850 psi | 13 mm/min; ASTM D790 |
| Flexural Modulus | 1.92 GPa | 278 ksi | 13 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.460 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
0.862 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded; ASTM D256 |
| Dart Drop Total Energy | 71.6 J/cm @Temperature 23.0 °C |
0.134 ft-lb/mil @Temperature 73.4 °F |
extruded profile, Procedure A, C.125; ASTM D4226 |
| >= 178 J/cm @Temperature 23.0 °C |
>= 0.333 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 75.0 µm/m-°C | 41.7 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 42.8 °C @Thickness 3.18 mm |
109 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| 43.9 °C @Thickness 3.18 mm |
111 °F @Thickness 0.125 in |
Annealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 37.8 °C @Thickness 3.18 mm |
100 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| 38.3 °C @Thickness 3.18 mm |
101 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 5.0 - 30 % | 5.0 - 30 % | 60°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 182 - 193 °C | 360 - 379 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Medium Gloss | |
| Forms | Pellets | |
| Generic Material | PVC, Semi-Rigid | |
| Generic Name | Polyvinyl Chloride, Semi-Rigid (PVC, Semi-Rigid) | |
| Processing Method | Coextrusion | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Capstock | |
| Outdoor Applications |
Users viewing this material also viewed the following:
- Network Polymers 779 Polystyrene
- Karina 450D18/199-D-AT-IS Gray PVC Compound
- Borealis HB306MO Polypropylene
- A. Schulman POLYBATCH™ Weatherwood 60190U Concentrate Based In LLDPE
- Dow Corning CY 52-276 KIT
- Arlon CP-410XD Bulk Compound
- Alliance C-7 Strontium Ferrite Ceramic Magnetic Material
- BASF Ultramid® A3L HP PA66 (Dry)
- Zhejiang Juner PC/ABSz-4 Alloy
- Polimeri Europa KOBLEND PCA 628 PC+ABS (discontinued **)
Copyright © lookpolymers.com All Rights Reserved