SABIC Innovative Plastics Noryl EUN0240 PPE+HIPS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) , Polystyrene + Polyphenylene Ether, Unreinforced , Polystyrene, Impact Modified |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Noryl EUN0240 PPE+HIPS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D 792 |
| Water Absorption | 0.070 % @Time 86400 sec |
0.070 % @Time 24.0 hour |
ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 37.0 MPa | 5370 psi | SABIC - Japan Method |
| Elongation at Break | 130 % | 130 % | SABIC - Japan Method |
| Flexural Strength | 54.0 MPa | 7830 psi | ASTM D 790 |
| Flexural Modulus | 2.05 GPa | 297 ksi | ASTM D 790 |
| Izod Impact, Notched | 2.94 J/cm @Temperature 23.0 °C |
5.51 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
38.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C @Thickness 3.20 mm |
230 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- NanoAmor 95%, OD: < 8 nm COOH Functionalized Aligned Multi-Walled Carbon Nanotubes
- Parker Chomerics Tecknit Teckshield®-F 100 OPI 0.002" Diameter Wire, Allycarbonate EMI Shielding Window
- Freudenberg Simrit V175 Aflasâ„¢ (TFE/P)
- LATI Laramid G/50 PPA, 50% Glass Fiber Reinforced
- Teknor Apex TEKBOND® 6700-45 Thermoplastic Elastomer
- Eastman Tenite 285A2R30020 Cellulose Acetate Butyrate, Natural, Trsp
- Akzo Nobel Trigonox® F-C50 Polymerization Initiator
- Mitsui Fybrel® UL 410 Polyolefin Synthetic Pulp, Wet Processes (discontinued **)
Copyright © lookpolymers.com All Rights Reserved