DuPont Performance Polymers Hytrel® 7246HS NC010 Polyester Elastomer TPC-ET  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer DuPont Performance Polymers
Trade Name Hytrel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Hytrel® 7246HS NC010 Polyester Elastomer TPC-ET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
72 Shore D High Performance Polyester Elastomer with Heat Ageing Protection Hytrel 7246HS NC010 is a high modulus heat stabilized grade with nominal hardness of 72D.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.25 g/cc
0.0452 lb/in³
ISO 1183
Mechanical Properties Metric English Comments
Hardness, Shore D 66
66
15s; ISO 868
<= 70
<= 70
ISO 868
Tensile Strength at Break 52.0 MPa
7540 psi
ISO 527-1/-2
Tensile Stress 23.0 MPa

@Strain 10.0 %
 3340 psi

@Strain 10.0 %
 ISO 527-1/-2
24.0 MPa

@Strain 50.0 %
 3480 psi

@Strain 50.0 %
 ISO 527-1/-2
5.55 MPa

@Strain 2.72 %,
Temperature 90.0 °C
 805 psi

@Strain 2.72 %,
Temperature 194 °F
 ISO 11403-1 -2
8.37 MPa

@Strain 2.14 %,
Temperature 40.0 °C
 1210 psi

@Strain 2.14 %,
Temperature 104 °F
 ISO 11403-1 -2
11.3 MPa

@Strain 2.00 %,
Temperature 23.0 °C
 1640 psi

@Strain 2.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
12.5 MPa

@Strain 10.9 %,
Temperature 90.0 °C
 1810 psi

@Strain 10.9 %,
Temperature 194 °F
 ISO 11403-1 -2
18.7 MPa

@Strain 8.56 %,
Temperature 40.0 °C
 2710 psi

@Strain 8.56 %,
Temperature 104 °F
 ISO 11403-1 -2
22.5 MPa

@Strain 1.80 %,
Temperature 0.000 °C
 3260 psi

@Strain 1.80 %,
Temperature 32.0 °F
 ISO 11403-1 -2
23.2 MPa

@Strain 8.00 %,
Temperature 23.0 °C
 3360 psi

@Strain 8.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
24.4 MPa

@Strain 1.57 %,
Temperature -20.0 °C
 3540 psi

@Strain 1.57 %,
Temperature -4.00 °F
 ISO 11403-1 -2
39.3 MPa

@Strain 7.20 %,
Temperature 0.000 °C
 5700 psi

@Strain 7.20 %,
Temperature 32.0 °F
 ISO 11403-1 -2
41.7 MPa

@Strain 12.6 %,
Temperature 0.000 °C
 6050 psi

@Strain 12.6 %,
Temperature 32.0 °F
 ISO 11403-1 -2
44.9 MPa

@Strain 6.28 %,
Temperature -20.0 °C
 6510 psi

@Strain 6.28 %,
Temperature -4.00 °F
 ISO 11403-1 -2
47.6 MPa

@Strain 11.0 %,
Temperature -20.0 °C
 6900 psi

@Strain 11.0 %,
Temperature -4.00 °F
 ISO 11403-1 -2
1.05 MPa

@Strain 0.516 %,
Time 3.60e+6 sec
 152 psi

@Strain 0.516 %,
Time 1000 hour
 isochronous; ISO 11403-1 -2
1.05 MPa

@Strain 0.556 %,
Time 3.60e+7 sec
 152 psi

@Strain 0.556 %,
Time 10000 hour
 isochronous; ISO 11403-1 -2
1.05 MPa

@Strain 0.444 %,
Time 36000 sec
 152 psi

@Strain 0.444 %,
Time 10.0 hour
 isochronous; ISO 11403-1 -2
1.05 MPa

@Strain 0.479 %,
Time 360000 sec
 152 psi

@Strain 0.479 %,
Time 100 hour
 isochronous; ISO 11403-1 -2
1.05 MPa

@Strain 0.412 %,
Time 3600 sec
 152 psi

@Strain 0.412 %,
Time 1.00 hour
 isochronous; ISO 11403-1 -2
2.00 MPa

@Strain 0.643 %,
Time 3.60e+7 sec
 290 psi

@Strain 0.643 %,
Time 10000 hour
 isochronous; ISO 11403-1 -2
2.00 MPa

@Strain 0.557 %,
Time 3600 sec
 290 psi

@Strain 0.557 %,
Time 1.00 hour
 isochronous; ISO 11403-1 -2
2.00 MPa

@Strain 0.641 %,
Time 360000 sec
 290 psi

@Strain 0.641 %,
Time 100 hour
 isochronous; ISO 11403-1 -2
2.00 MPa

@Strain 0.642 %,
Time 3.60e+6 sec
 290 psi

@Strain 0.642 %,
Time 1000 hour
 isochronous; ISO 11403-1 -2
2.00 MPa

@Strain 0.614 %,
Time 36000 sec
 290 psi

@Strain 0.614 %,
Time 10.0 hour
 isochronous; ISO 11403-1 -2
4.20 MPa

@Strain 2.00 %,
Time 36000 sec
 609 psi

@Strain 2.00 %,
Time 10.0 hour
 isochronous; ISO 11403-1 -2
4.20 MPa

@Time 3600 sec,
Strain 1.83 %
 609 psi

@Time 1.00 hour,
Strain 1.83 %
 isochronous; ISO 11403-1 -2
4.20 MPa

@Strain 2.35 %,
Time 3.60e+6 sec
 609 psi

@Strain 2.35 %,
Time 1000 hour
 isochronous; ISO 11403-1 -2
4.20 MPa

@Strain 2.52 %,
Time 3.60e+7 sec
 609 psi

@Strain 2.52 %,
Time 10000 hour
 isochronous; ISO 11403-1 -2
4.20 MPa

@Strain 2.18 %,
Time 360000 sec
 609 psi

@Strain 2.18 %,
Time 100 hour
 isochronous; ISO 11403-1 -2
8.00 MPa

@Strain 3.11 %,
Time 3.60e+6 sec
 1160 psi

@Strain 3.11 %,
Time 1000 hour
 isochronous; ISO 11403-1 -2
8.00 MPa

@Strain 2.98 %,
Time 360000 sec
 1160 psi

@Strain 2.98 %,
Time 100 hour
 isochronous; ISO 11403-1 -2
8.00 MPa

@Time 3600 sec,
Strain 2.46 %
 1160 psi

@Time 1.00 hour,
Strain 2.46 %
 isochronous; ISO 11403-1 -2
8.00 MPa

@Strain 3.22 %,
Time 3.60e+7 sec
 1160 psi

@Strain 3.22 %,
Time 10000 hour
 isochronous; ISO 11403-1 -2
8.00 MPa

@Strain 2.76 %,
Time 36000 sec
 1160 psi

@Strain 2.76 %,
Time 10.0 hour
 isochronous; ISO 11403-1 -2
8.40 MPa

@Strain 5.68 %,
Time 36000 sec
 1220 psi

@Strain 5.68 %,
Time 10.0 hour
 isochronous; ISO 11403-1 -2
8.40 MPa

@Strain 6.81 %,
Time 3.60e+6 sec
 1220 psi

@Strain 6.81 %,
Time 1000 hour
 isochronous; ISO 11403-1 -2
8.40 MPa

@Time 3600 sec,
Strain 4.98 %
 1220 psi

@Time 1.00 hour,
Strain 4.98 %
 isochronous; ISO 11403-1 -2
8.40 MPa

@Strain 6.32 %,
Time 360000 sec
 1220 psi

@Strain 6.32 %,
Time 100 hour
 isochronous; ISO 11403-1 -2
8.40 MPa

@Strain 7.26 %,
Time 3.60e+7 sec
 1220 psi

@Strain 7.26 %,
Time 10000 hour
 isochronous; ISO 11403-1 -2
16.0 MPa

@Strain 10.5 %,
Time 3.60e+6 sec
 2320 psi

@Strain 10.5 %,
Time 1000 hour
 isochronous; ISO 11403-1 -2
16.0 MPa

@Strain 7.73 %,
Time 36000 sec
 2320 psi

@Strain 7.73 %,
Time 10.0 hour
 isochronous; ISO 11403-1 -2
16.0 MPa

@Strain 12.1 %,
Time 3.60e+7 sec
 2320 psi

@Strain 12.1 %,
Time 10000 hour
 isochronous; ISO 11403-1 -2
16.0 MPa

@Time 3600 sec,
Strain 6.63 %
 2320 psi

@Time 1.00 hour,
Strain 6.63 %
 isochronous; ISO 11403-1 -2
16.0 MPa

@Strain 9.05 %,
Time 360000 sec
 2320 psi

@Strain 9.05 %,
Time 100 hour
 isochronous; ISO 11403-1 -2
Tensile Strength, Yield 29.0 MPa
4210 psi
ISO 527-1/-2
Elongation at Break >= 300 %
>= 300 %
ISO 527-1/-2
560 %
560 %
Nominal; ISO 527-1/-2
Elongation at Yield 22 %
22 %
ISO 527-1/-2
Tensile Modulus 0.430 GPa
62.4 ksi
ISO 527-1/-2
0.256 GPa

@Temperature 110 °C
 37.1 ksi

@Temperature 230 °F
 Dynamic; ISO 11403-1 -2
0.837 GPa

@Temperature 30.0 °C
 121 ksi

@Temperature 86.0 °F
 Dynamic; ISO 11403-1 -2
2.33 GPa

@Temperature -20.0 °C
 339 ksi

@Temperature -4.00 °F
 Dynamic; ISO 11403-1 -2
3.53 GPa

@Temperature -70.0 °C
 511 ksi

@Temperature -94.0 °F
 Dynamic; ISO 11403-1 -2
4.47 GPa

@Temperature -100 °C
 648 ksi

@Temperature -148 °F
 Dynamic; ISO 11403-1 -2
Flexural Modulus 0.500 GPa
72.5 ksi
ISO 178
Shear Modulus 0.0455 GPa

@Temperature 160 °C
 6.60 ksi

@Temperature 320 °F
 Dynamic; ISO 11403-1 -2
0.0580 GPa

@Temperature 120 °C
 8.41 ksi

@Temperature 248 °F
 Dynamic; ISO 11403-1 -2
0.0787 GPa

@Temperature 70.0 °C
 11.4 ksi

@Temperature 158 °F
 Dynamic; ISO 11403-1 -2
0.307 GPa

@Temperature 20.0 °C
 44.5 ksi

@Temperature 68.0 °F
 Dynamic; ISO 11403-1 -2
0.764 GPa

@Temperature -20.0 °C
 111 ksi

@Temperature -4.00 °F
 Dynamic; ISO 11403-1 -2
0.979 GPa

@Temperature -50.0 °C
 142 ksi

@Temperature -58.0 °F
 Dynamic; ISO 11403-1 -2
Shear Strength 0.109 MPa

@Shear Rate 500 1/s,
Temperature 260 °C
 15.8 psi

@Shear Rate 500 1/s,
Temperature 500 °F
 ISO 11403-1 -2