PolyOne Edgetek® SF-35GF-25MN/000 Polyphenylene Sulfide (PPS), Glass/Mineral Filled (discontinued **)
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® SF-35GF-25MN/000 Polyphenylene Sulfide (PPS), Glass/Mineral Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass/Mineral ReinforcedUL 94 V0 (HEM TEST)PolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.88 g/cc | 1.88 g/cc | ASTM D792 |
| Water Absorption | 0.030 % | 0.030 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 114 MPa | 16500 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 15.2 GPa | 2200 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 172 MPa | 25000 psi | ASTM D790 |
| Flexural Modulus | 15.2 GPa | 2200 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.50 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | Annealed, 0.125 in bars; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 299 - 332 °C | 570 - 630 °F | Molding |
| Mold Temperature | 135 - 149 °C | 275 - 300 °F | |
| Drying Temperature | 135 - 149 °C | 275 - 300 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Rogers Corporation Bisco™ HT-1200 Solid Silicone Rubber
- Premix Thermoplastics PRE-ELEC® CP 1315 (discontinued **)
- Chevron Phillips Marlex® HHM TR-140 Polyethylene, Film Grade; HDPE (discontinued **)
- SABIC Innovative Plastics NORYL WCD915 PPE-TPE (Asia Pacific)
- Shuman SP930 White Polycarbonate
- Teknor Apex APEX® SRP 2700A Polyvinyl Chloride, Rigid
- Borealis Borstar® FB2230 LLDPE for Film
- ExxonMobil Bicor™ 40MB666 OPP Film
- ExxonMobil LLDPE LL 3003.32 Linear Low Density Polyethylene Resin
Copyright © lookpolymers.com All Rights Reserved