PolyOne Edgetek® PI-10GF/000 Polyetherimide (PEI), Glass Filled (discontinued **)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® PI-10GF/000 Polyetherimide (PEI), Glass Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0050 cm/cm | 0.0040 - 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 112 MPa | 16200 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 4.14 GPa | 600 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 124 MPa | 18000 psi | ASTM D790 |
| Flexural Modulus | 4.83 GPa | 700 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.00 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 18.0 µm/m-°C @Temperature 20.0 °C |
10.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 343 - 371 °C | 650 - 700 °F | Molding |
| Mold Temperature | 135 - 149 °C | 275 - 300 °F | |
| Drying Temperature | 149 °C | 300 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Old Hickory UltraCast Slurry PC-2034 Kentucky Ball Clay
- Lucent Polymers TPP-230 Polypropylene, 30% Talc Filled, Impact Modified
- SolVin 367NC Polyvinyl Chloride Low Viscosity Paste
- Teknor Apex Sinvicomp SFE 3500 Polyvinyl Chloride, Flexible
- Borealis BorSafe™ ME3445 Medium Density Polyethylene
- ExxonMobil 100 Mobiltemp SHC Series
- Axiall 9149 Wire & Cable Flexible PVC
- ATI Wah Chang Niobium
Copyright © lookpolymers.com All Rights Reserved