Dow AFFINITY™ PF 1140G Polyolefin Plastomer (POP)

Category Polymer , Film , Thermoplastic , Polyolefin
Manufacturer Dow Chemical
Trade Name AFFINITY™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow AFFINITY™ PF 1140G Polyolefin Plastomer (POP).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AFFINITY™ PF 1140G is an ethylene alpha-olefin resin produced via INSITE™ Technologies. It is designed to be used in a variety of demanding applications including form-fill-seal packaging and fresh produce bags. This resin has excellent compatibility with other polyolefins, allowing efficient blending and co-extrusion.Information provided by Dow
Physical Properties Metric English Comments
Density 0.8965 g/cc
0.03239 lb/in³
ASTM D792
Thickness 50.8 microns
2.00 mil
Melt Flow 1.6 g/10 min
1.6 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 5.79 MPa
840 psi
ASTM D882
Film Tensile Strength at Yield, TD 6.34 MPa
920 psi
ASTM D882
Film Elongation at Break, MD 690 %
690 %
ASTM D882
Film Elongation at Break, TD 700 %
700 %
ASTM D882
Secant Modulus, MD 0.0730 GPa
10.6 ksi
2% Secant; ASTM D882
Secant Modulus, TD 0.0730 GPa
10.6 ksi
2% Secant; ASTM D882
Impact 18.8
18.8
[lb<sub>f</sub>]; Puncture Resistance Force; Dow Method
245
245
[ft-lbf/in<sup>3</sup>]; Puncture Resistance; Dow Method
Puncture Energy 8.18 J
6.03 ft-lb
Dow Method
Elmendorf Tear Strength MD 470 g
470 g
Modified rectangular test specimen; ASTM D1922
Elmendorf Tear Strength TD 620 g
620 g
Modified rectangular test specimen; ASTM D1922
Elmendorf Tear Strength, MD 9.25 g/micron
235 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 12.2 g/micron
310 g/mil
ASTM D1922
Dart Drop Test >= 850 g
>= 1.87 lb
Method B; ASTM D1709
Film Tensile Strength at Break, MD 50.3 MPa
7290 psi
ASTM D882
Film Tensile Strength at Break, TD 39.5 MPa
5730 psi
ASTM D882
Heat Seal Strength Initiation Temperature 81.0 °C
178 °F
2 lb/in heat seal strength; 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method
Thermal Properties Metric English Comments
Melting Point 96.0 °C
205 °F
Dow Method (DSC)
Vicat Softening Point 77.0 °C
171 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 1.3 %
1.3 %
ASTM D1003
Gloss 134 %
134 %
20°; ASTM D2457
Transmission, Visible 70 %
70 %
Clarity; ASTM D1746