PolyOne Edgetek® PC-20GF/000 Polycarbonate (PC)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | PolyOne Corporation |
| Trade Name | Edgetek® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® PC-20GF/000 Polycarbonate (PC).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | @ 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 85 | 85 | ASTM D785 |
| Tensile Strength at Break | 107 MPa | 15500 psi | Type I, 5.1 mm/min; ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 6.89 GPa | 999 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 131 MPa | 19000 psi | ASTM D790 |
| Flexural Modulus | 5.52 GPa | 801 ksi | ASTM D790 |
| Compressive Strength | 141 MPa | 20500 psi | ASTM D695 |
| Shear Strength | 58.6 MPa | 8500 psi | ASTM D732 |
| Izod Impact, Notched | 1.30 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
2.44 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 29.0 µm/m-°C | 16.1 µin/in-°F | ASTM D696 |
| Thermal Conductivity | 0.340 W/m-K | 2.36 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 149 °C @Thickness 3.18 mm |
300 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 143 °C @Thickness 3.18 mm |
289 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| Flammability, UL94 | V-1 | V-1 | UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 6.00e+15 ohm-cm | 6.00e+15 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 288 - 316 °C | 550 - 601 °F | |
| Mold Temperature | 82.2 - 121 °C | 180 - 250 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 2.00 hour | 2.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Filler / Reinforcement | Glass Fiber Reinforcement | |
| Forms | Pellets | |
| Generic Material | PC | |
| Generic Name | Polycarbonate (PC) | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America |
Users viewing this material also viewed the following:
- Radici Radilon® A ECP3808 (cond.) Nylon 66
- Solvay Technyl® C218V30 30% Glass Filled, Heat Stabilized Nylon 6
- SABIC Innovative Plastics ULTEM 2410R PEI (Asia Pacific)
- Shandong Dongyue Polymer DF-201 PTFE Fine Powder
- Silberline Silvet® 210-20-J
- SABIC Innovative Plastics LNP THERMOCOMP RF003ES PA 66
- A. Schulman LP481 Molding Grade High-Density Polyethylene
- Eastman Aspira EB062 Copolyester Resin for Extrusion Blown Bottles
- Amity Thermosets ATM 123 Phenolic Molding Organic Filler, Compression Molded
- Addiplast Addinyl B2H M30 Flame Retardant Nylon 6, 30% Mineral Filled
Copyright © lookpolymers.com All Rights Reserved