PolyOne Edgetek® ATH-15GF/000 Acetal-Homopolymer, Glass Filled (discontinued **)
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® ATH-15GF/000 Acetal-Homopolymer, Glass Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.51 g/cc | 1.51 g/cc | ASTM D792 |
| Water Absorption | 0.20 % @Thickness 3.17 mm |
0.20 % @Thickness 0.125 in |
24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0060 cm/cm | 0.0050 - 0.0060 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 66.9 MPa | 9700 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 4.83 GPa | 700 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 66.9 MPa | 9700 psi | ASTM D790 |
| Flexural Modulus | 4.83 GPa | 700 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.00 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 199 - 216 °C | 390 - 420 °F | Molding |
| Mold Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Drying Temperature | 65.6 °C | 150 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Pasargad Polymer Peyvand Pasalac 3P-H6000B ABS
- SABIC Innovative Plastics ULTEM HU2210 PEI
- Shin-Etsu Silicones FE-381U Fluorosilicone Elastomer
- SABIC Innovative Plastics LNP STAT-KON TE002 PU
- Styron CALIBREâ„¢ 7100-8 Polycarbonate
- Fainplast Compounds GS 61/R Flexible PVC, Injection Molding for Footwear
- Barlog Plastics KEBAPEAK XS1700 PEEK, unreinforced
- Ametek Ultra 316L P/M Stainless Steel, Sintered from 6.22 g/cc Green Density
- Aremco Aremco-Bond™ 2220 High Performance Epoxide
Copyright © lookpolymers.com All Rights Reserved