PolyOne Edgetek® AS-20CF/000 Acrylonitrile Butadiene Styrene (ABS), Carbon Fiber Reinforced (discontinued **)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® AS-20CF/000 Acrylonitrile Butadiene Styrene (ABS), Carbon Fiber Reinforced
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Carbon Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0015 cm/cm | 0.0010 - 0.0015 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 89.6 MPa | 13000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 5.86 GPa | 850 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 117 MPa | 17000 psi | ASTM D790 |
| Flexural Modulus | 5.86 GPa | 850 ksi | ASTM D790 |
| Izod Impact, Notched | 0.854 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.60 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 100 - 10000 ohm-cm | 100 - 10000 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 100 - 10000 ohm | 100 - 10000 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 221 - 243 °C | 430 - 470 °F | Molding |
| Mold Temperature | 60.0 - 71.1 °C | 140 - 160 °F | |
| Drying Temperature | 60.0 - 71.1 °C | 140 - 160 °F | |
| Dry Time | 6 hour | 6 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- SABIC HP4023W Low Density Polyethylene for Blown Film
- Kinetics MIM 420 Stainless Steel (Oil Quench Heat Treat)
- Mitsubishi Xantar® FC 22 UR Polycarbonate
- SABIC Innovative Plastics Ultem 2313 PEI (Asia Pacific)
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 0.20 PHR Caytur 4
- CMT Materials HYTAC® FLX Good Durability, Easily Machined & Polished Copolymer Syntactic
- ConocoPhillips El Mar® Grade 15W-40 Geo Oil
- Barlog Plastics KEBAFORM C 909 WR POM Copolymer unreinforced, UV-stabilized
- Armstrong A-706 Epoxy Adhesive
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR N650 Filler
Copyright © lookpolymers.com All Rights Reserved