Polimeri Europa Eraclene® MP 94 High Density Polyethylene - Injection Molding

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded
Manufacturer	Polimeri Europa (Former EniChem)
Trade Name	Eraclene®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polimeri Europa Eraclene® MP 94 High Density Polyethylene - Injection Molding.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Eraclene MP 94 is a high density polyethylene homopolymer resin (HDPE) with antioxidants, suitable for injection molding application.This resin has a narrow molecular weight distribution and a high density which makes it the perfect choice for the manufacturing of items requiring outstanding rigidity, warpage resistance and toughness. Eraclene MP 94 is UV stabilized and is recommended for the production of items for outdoor exposure.Main Applications: Eraclene MP 94 is specifically designed for molded crates, cases, toys, trays and other similar objects requiring rigidity.Information provided by Polimeri Europa.

Physical Properties	Metric	English	Comments
Specific Gravity	0.960 g/cc	0.960 g/cc	ISO 1183
Melt Flow	7.0 g/10 min @Load 2.16 kg, Temperature 190 °C	7.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
	20 g/10 min @Load 5.00 kg, Temperature 190 °C	20 g/10 min @Load 11.0 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	69	69	ISO 868/A
Tensile Strength at Break	17.0 MPa	2470 psi	ISO 527
Tensile Strength, Yield	30.0 MPa	4350 psi	ISO 527
Elongation at Break	400 %	400 %	ISO 527
Flexural Modulus	1.45 GPa	210 ksi	ISO 178
Izod Impact, Notched	1.00 J/cm	1.87 ft-lb/in	ISO 180/A

Thermal Properties	Metric	English	Comments
Melting Point	137 °C	279 °F	Internal method
Vicat Softening Point	128 °C @Load 1.00 kg	262 °F @Load 2.20 lb	ISO 306/A
Brittleness Temperature	<= -60.0 °C	<= -76.0 °F	ASTM D746