ExxonMobil Label-Lyte™ 38LW280 OPP Film

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer Exxon Chemical
Trade Name Label-Lyte™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Label-Lyte™ 38LW280 OPP Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: A super white opaque slip controlled, biaxially oriented polypropylene film, metalized on one side. Designed for use in reel-fed wrap-around applications, where outstanding metalized appearance and superior graphics are desired.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Brilliant metal appearanceExcellent adhesion of aluminum to filmSlip controlled unmetallized surfaceHigh tear and split resistanceHigh resistance to elongation on labeling machineExcellent stiffnessExcellent mechanical propertiesGood mold resistanceApplications: Beverage, AlcoholicBeverage, Carbonated Beverage, Mineral Waters Dairy ProductsHealth and Beauty CareHousehold and DetergentsIndustrial Uses: Reel-Fed LabelsProcessing Method: Inner Web Adhesion Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil
Physical Properties Metric English Comments
Thickness 38.1 microns
1.50 mil
ExxonMobil Method
Coating Weight 23.2 g/m²
14.5 lb/ream
ExxonMobil Method
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 140 %
140 %
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Elongation at Break, TD 50 %
50 %
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Modulus of Elasticity 1.30 GPa
189 ksi
MD; ExxonMobil Method
2.10 GPa
305 ksi
TD; ExxonMobil Method
Coefficient of Friction 0.40
0.40
Untreated Surface; ExxonMobil Method
Film Tensile Strength at Break, MD 100 MPa
14500 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD 155 MPa
22500 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Thermal Properties Metric English Comments
Shrinkage, MD 6.0 %

@Temperature 135 °C,
Time 432 sec
6.0 %

@Temperature 275 °F,
Time 0.120 hour
ExxonMobil Method
Shrinkage, TD 6.0 %

@Temperature 135 °C,
Time 432 sec
6.0 %

@Temperature 275 °F,
Time 0.120 hour
ExxonMobil Method
Optical Properties Metric English Comments
Optical Density 1.9
1.9
ExxonMobil Method
Gloss 75 %
75 %
45°; ExxonMobil Method
Descriptive Properties Value Comments
Yield 29800 in2/lb