PlastxWorld CEVIAN® A1700 PA/ABS Alloy, Conditioned
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend , Nylon |
| Manufacturer | PlastxWorld, Inc. |
| Trade Name | CEVIAN® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PlastxWorld CEVIAN® A1700 PA/ABS Alloy, Conditioned.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Property data is for samples at equilibrium moisture (2.0%)Information provided by PlastxWorld Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | ASTM D792 |
| Water Absorption | 0.98 % | 0.98 % | 24 hr; ASTM D570 |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 109 | 109 | ASTM D785 |
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | ASTM 638 |
| Elongation at Break | >= 200 % | >= 200 % | ASTM D635 |
| Flexural Yield Strength | 46.2 MPa | 6700 psi | ASTM D790 |
| Flexural Modulus | 0.814 GPa | 118 ksi | ASTM D790 |
| Izod Impact, Notched | 4.32 J/cm @Thickness 3.17 mm |
8.10 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 99.0 °C | 210 °F | 0.25 inch; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C | 172 °F | 0.25 inch; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycolac® FR15 ABS (Asia Pacific)
- Kolon SPESIN® KP513FLBL Multi Reinforced PBT Resin (discontinued **)
- Nilit RECONYL A KV30 Recycled nylon 6.6 for injection molding, 30% glass ball reinforced
- Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet
- Solvay TECHNYL® A 218 V30 Black 21 NHFE PA66, 30% glass fiber, DRY
- A. Schulman POLYBLAK™ 4676 Black Color Concentrate, 50% Carbon Black Based In LLDPE
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 83A
- Azdel SuperLite® SL551200-100 PP Resin Matrix / 55% Glass Fiber (7 mm Molded Thickness)
Copyright © lookpolymers.com All Rights Reserved