- Plastcom PLASTALEN® PQ 81 T 15/1 Polypropylene reinforced with mineral filler, impact modified
Plastcom PLASTALEN® PQ 81 T 15/1 Polypropylene reinforced with mineral filler, impact modified
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced, Impact Modified |
| Manufacturer | Plastcom spol. s r.o. |
| Trade Name | PLASTALEN® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Plastcom PLASTALEN® PQ 81 T 15/1 Polypropylene reinforced with mineral filler, impact modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Modified PP for injection molding with the content of 15% mineral filler. Application in automotive industry. Delivered in black grade.Information Provided by Plastcom spol. s r.o.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | STN EN ISO 1183-1 |
| Filler Content | 15 % | 15 % | |
| Linear Mold Shrinkage | 0.0111 cm/cm | 0.0111 in/in | STN EN ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | STN EN ISO 294-4 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
STN EN ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 15.0 MPa | 2180 psi | STN EN ISO 527-2 |
| Elongation at Break | 6.0 % | 6.0 % | STN EN ISO 527-2 |
| Tensile Modulus | 1.10 GPa | 160 ksi | STN EN ISO 527-2 |
| Flexural Strength | 17.0 MPa | 2470 psi | STN EN ISO 178 |
| Flexural Modulus | 1.02 GPa | 148 ksi | STN EN ISO 178 |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
STN EN ISO 179 |
| NB @Temperature -20.0 °C |
NB @Temperature -4.00 °F |
STN EN ISO 179 | |
| Charpy Impact, Notched | 4.80 J/cm² @Temperature -20.0 °C |
22.8 ft-lb/in² @Temperature -4.00 °F |
STN EN ISO 179 |
| 7.50 J/cm² @Temperature 23.0 °C |
35.7 ft-lb/in² @Temperature 73.4 °F |
STN EN ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | STN EN ISO 75-2 (A) |
| Vicat Softening Point | 115 °C | 239 °F | STN EN ISO 306 |
| Flammability, UL94 | HB | HB |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 - 250 °C | 392 - 482 °F | |
| Mold Temperature | 40.0 - 70.0 °C | 104 - 158 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.10 % | 0.10 % | STN EN ISO 3344 |
| Injection Pressure | 70.0 - 120 MPa | 10200 - 17400 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black |
Users viewing this material also viewed the following:
- Polimeri Europa Extir® A 7000 AE Expandable Polystyrene, Standard Flame Retardant
- BASF Capron® HPN 9333G Impact Modified, 33% Glass-Filled Nylon 6 (Dry) (discontinued **)
- Sylvin Technologies 9077-80 LMW Natural PVC for Injection Molding
- SABIC Innovative Plastics LNP LUBRILOY D2000P PC (Asia Pacific)
- SABIC Innovative Plastics Valox® EH7020 PBT (Asia Pacific)
- Sharadaa Ceramics ZAP 009 Smart Cast Application
- SABIC Innovative Plastics LNP STAT-KON DX05305C PC
- Diamond Polymers PC 1001 GF30 30% Glass Reinforced Polycarbonate
- DuPont Teijin Films Mylar® CL Polyester Film, 50 Gauge
Copyright © lookpolymers.com All Rights Reserved