Petroquimica Triunfo Trilene® TS 8056 LLDPE-C8 and LDPE Blend

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , LLDPE
Manufacturer Petroquimica Triunfo
Trade Name Trilene®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Petroquimica Triunfo Trilene® TS 8056 LLDPE-C8 and LDPE Blend.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The Trilene TS 8056 product is a blend with a high ratio of linear low-density polyethylene - octene comonomer (LLDPE-C8) with low-density polyethylene (LDPE) with elevated processability, ensuring the production of films with uniform thickness and good visual appearance and weldability. This product presents excellent puncture resistance, exactly to the low temperatures, what it becomes it especially adequate the production of packings for frozen products, as cuts of meat and chicken with or without bone, fish, seafood and ice. The additive package gives it thermal stability, low blocking, and adequate slip performance, which are indispensable to allow high productivity on the extrusion, printing, and finishing lines. The resin should be processed in extruders that are designed or adapted for LLDPE. The components that form the product Trilene TS 8056 complies with the requirements of Brazilian and corresponding legislation of Mercosul and it is in conformity with FDA Regulations 21 CFR 177.1520 (c) 2.1, to contact with foodstuff.Applications: Technical laminated films designed for packaging of various products such as coffee, crackers, etc. Technical films for automatic or semi-automatic packaging of solid products (grains, powdered, etc.), liquids (milk, yot, etc.), and frozen foods (poultry, beef cuts, seafood, ice, etc.).Resin Properties: Compressed molded plate. Method ASTM D-1928, procedure C. Film obtained on a 50mm blow film line with barrier screw, 25:1 L/D, 1.0mm die gap, 50µm gauge, 2.3:1 BUR.Information provided by Dax Resinas
Physical Properties Metric English Comments
Density 0.920 g/cc
0.0332 lb/in³
ASTM D1505
Thickness 50.0 microns
1.97 mil
Melt Index of Compound 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 790 %
790 %
ASTM D882
Film Elongation at Break, TD 890 %
890 %
ASTM D882
Secant Modulus, MD 0.0930 GPa
13.5 ksi
5%; ASTM D882
Secant Modulus, TD 0.0970 GPa
14.1 ksi
5%; ASTM D882
Coefficient of Friction, Dynamic 0.090
0.090
ASTM D1894
Elmendorf Tear Strength, MD 13.2 g/micron
335 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 13.2 g/micron
335 g/mil
ASTM D1922
Dart Drop Test 300 g
0.662 lb
(method A); ASTM D1709
Film Tensile Strength at Break, MD 32.0 MPa
4640 psi
ASTM D882
Film Tensile Strength at Break, TD 29.0 MPa
4210 psi
ASTM D882
Optical Properties Metric English Comments
Haze 7.5 %
7.5 %
ASTM D1003
Gloss 113 %
113 %
@ 60° Gardner; ASTM D2457
Processing Properties Metric English Comments
Processing Temperature 180 - 190 °C
356 - 374 °F
Plasticizing Zone
190 - 200 °C
374 - 392 °F
Mixture Zone
Feed Temperature 170 - 180 °C
338 - 356 °F
Adapter Temperature 180 - 200 °C
356 - 392 °F
Die Cooling Temperature 200 - 220 °C
392 - 428 °F
Die Opening 0.180 - 0.250 cm
0.0709 - 0.0984 in
Blow-up Ratio (BUR) 3.0
3.0
Recommended
Descriptive Properties Value Comments
Proportion LLDPE % 75
PTN-570-Q