Techmer ES HiFill® PA6/6 CC20 Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® PA6/6 CC20 Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Calcium Carbonate Filler, 20% Filler by WeightInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ASTM D792 |
| Water Absorption | 0.85 % @Time 86400 sec |
0.85 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.012 cm/cm @Thickness 3.17 mm |
0.012 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 82.7 MPa | 12000 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 124 MPa | 18000 psi | ASTM D790 |
| Flexural Modulus | 4.14 GPa | 600 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm @Thickness 3.17 mm |
0.800 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 52.2 µm/m-°C | 29.0 µin/in-°F | ASTM D696 |
| Melting Point | 254 °C | 490 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 252 °C | 485 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 3.00e+14 ohm-cm | 3.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 20.5 kV/mm | 520 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Ineos L12Z-01 Polypropylene Impact Copolymer
- MTI ThermoStran® TPU-50G Long Glass Fiber Compound
- Sylvin Technologies 9999-60 Natural PVC Molding Compound
- SABIC Innovative Plastics LNP THERMOCOMP EF004 PEI
- Master Bond MB600SCN Aqueous Based Electrically Conductive Sodium Silicate Coating
- 3M 34383 General Purpose Aluminum Foil Tape
- Arlon R36338R015 0.0155" (0.394 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- 3M Top Line Pre-Burnish Floor Conditioner
- Honeywell MAP-Shield™ AF Generation 2 Shrinkable Barrier Film (discontinued **)
- Adell AH-18 Nylon 66, 40% Mineral Filled
Copyright © lookpolymers.com All Rights Reserved