Permabond TA4300 Toughened Acrylic Adhesive

Category	Polymer , Adhesive , Thermoset , Acrylic/Cyanoacrylate Adhesive
Manufacturer	Permabond
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Permabond TA4300 Toughened Acrylic Adhesive.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

PERMABOND® TA4300 is a 2-part, 1:1 toughened acrylic adhesive. Its toughening makes it ideal for bonding dissimilar materials where differential thermal expansion and contraction could be an issue. It cures rapidly at room temperature and has good gap filling properties. It is ideal for use on a variety of metals and gives particularly high bond strength on aluminum surfaces. Features & Benefits: Adhesion to a wide variety of substrates Fast cure at room temperature Easy to apply through static mixer nozzle High shear and peel strength Good impact strength Good chemical resistance Information provided by Permabond.

Physical Properties	Metric	English	Comments
Density	1.05 g/cc	0.0379 lb/in³	TA4300A
	1.05 g/cc	0.0379 lb/in³	TA4300B
Storage Temperature	2.00 - 7.00 °C	35.6 - 44.6 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength	22.0 - 24.0 MPa	3190 - 3480 psi	DIN 53288
Adhesive Bond Strength	20.0 - 22.0 MPa	2900 - 3190 psi	Mild steel, Shear
Peel Strength	6.00 - 7.20 kN/m	34.2 - 41.1 pli	ISO 4578

Thermal Properties	Metric	English	Comments
CTE, linear	80.0 µm/m-°C	44.4 µin/in-°F	ASTM D696
Thermal Conductivity	0.100 W/m-K	0.694 BTU-in/hr-ft²-°F	ASTM C177

Electrical Properties	Metric	English	Comments
Volume Resistivity	2.00e+13 ohm-cm	2.00e+13 ohm-cm	ASTM D257
Dielectric Constant	4.6 @Frequency 1.00e+7 Hz	4.6 @Frequency 1.00e+7 Hz	ASTM D150
Dielectric Strength	30.0 - 50.0 kV/mm	762 - 1270 kV/in	ASTM D149

Processing Properties	Metric	English	Comments
Cure Time	4.98 - 10.0 min	0.0830 - 0.167 hour	handling time
	15.0 - 30.0 min	0.250 - 0.500 hour	working strength
	1440 min	24.0 hour	full cure
Shelf Life	12.0 Month	12.0 Month

Descriptive Properties	Value	Comments
Appearance	Brown TA4300B, Thixotropic paste	Uncured
	Off-white TA4300A, Thixotropic paste	Uncured
Maximum Gap Fill (mm)	2
Strength Retention	100% at 0°C	Relative to 0°C
	15% at 175°C	Relative to 0°C
	22% at 150°C	Relative to 0°C
	80% at 100°C	Relative to 0°C
	96% at 50°C	Relative to 0°C