Sharadaa Ceramics REFCAST K SUPER High Alumina Castables
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Sharadaa Ceramics |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sharadaa Ceramics REFCAST K SUPER High Alumina Castables.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: We bring to our clients a qualitative range of Dense Alumina Castables that are conventional castable of medium purity. These castables cater to the application needs of various industries such as steel, cement, petrochemical and non-ferrous industries.Information provided by Sharadaa Ceramics Pvt. Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | >= 2.00 g/cc | >= 0.0723 lb/in³ | Dried at 110°C |
| Grain Size | <= 5000 µm | <= 5000 µm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.00294 GPa @Temperature 1100 °C |
0.426 ksi @Temperature 2010 °F |
|
| 0.00637 GPa @Temperature 110 °C |
0.924 ksi @Temperature 230 °F |
||
| 0.00883 GPa @Temperature 1500 °C |
1.28 ksi @Temperature 2730 °F |
||
| Compressive Strength | 34.3 MPa @Temperature 1100 °C |
4980 psi @Temperature 2010 °F |
Cold Crushing |
| 49.0 MPa @Temperature 110 °C |
7110 psi @Temperature 230 °F |
Cold Crushing | |
| 58.8 MPa @Temperature 1500 °C |
8530 psi @Temperature 2730 °F |
Cold Crushing | |
| 24.5 MPa @Time 86400 sec |
3560 psi @Time 24.0 hour |
Cold Crushing |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.930 W/m-K @Temperature 400 °C, Time 10800 sec |
6.45 BTU-in/hr-ft²-°F @Temperature 752 °F, Time 3.00 hour |
|
| 0.988 W/m-K @Temperature 600 °C, Time 10800 sec |
6.86 BTU-in/hr-ft²-°F @Temperature 1110 °F, Time 3.00 hour |
||
| 1.10 W/m-K @Temperature 800 °C, Time 10800 sec |
7.63 BTU-in/hr-ft²-°F @Temperature 1470 °F, Time 3.00 hour |
||
| Maximum Service Temperature, Air | 1550 °C | 2820 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | >= 60 % | >= 60 % | |
| Fe2O3 | <= 1.0 % | <= 1.0 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Permanent Linear Change | <-0.12 | 800°C |
| <-0.19 | 1100°C | |
| <-1.2 | 1500°C | |
| Refractoriness | 1680°C | |
| Thermal Expansion | 0.6 | Reversible |
| Water Required to Mix | 9-11% |
Users viewing this material also viewed the following:
- Kennametal Stellite Nistelle 718 Nickel Superalloy
- SABIC Innovative Plastics LNP STAT-LOY Cycoloy_CA6200 PC+ABS
- Stir SpA TP 78 GE OIL (PVC)
- SABIC Innovative Plastics NORYL GTX GTX914 PPE+PA
- Teknor Apex APEX® 80328-Y Polyvinyl Chloride, Flexible
- A. Schulman POLYFORT™ FPP 1640 Glass Reinforced, Mineral Fortified Homopolymer Polypropylene
- Polyram Bondyram® TL4101B Maleic Anhydride Modified Linear Low Density Polyethylene
- DuPont™ Appeel® 22D843 Ethylene Acrylate
- Teknor Apex APEX® 3202-60 Polyvinyl Chloride, Flexible
- Haynes 25 alloy, room temperature after 10% cold reduction, 1175°C anneal for 5 minutes
Copyright © lookpolymers.com All Rights Reserved