Parker Chomerics CHO-SEAL 6370 Conductive Elastomer

Category	Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) , Silicone
Manufacturer	Parker Chomerics
Trade Name	CHO-SEAL
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Parker Chomerics CHO-SEAL 6370 Conductive Elastomer.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Commercial Grade Conductive Elastomer Extrusions. These materials offer excellent cost/performance characteristics for commercial EMI gasket applications. These silicone and fluorosilicone based conductive elastomer materials offer excellent resistance to compression set over a wide temperature range, resulting in years of continuous service.Extruded onlyInformation provided by Chomerics

Physical Properties	Metric	English	Comments
Specific Gravity	1.85 - 2.35 g/cc	1.85 - 2.35 g/cc	ASTM D792

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	50 - 70	50 - 70	ASTM D2240
Tensile Strength at Break	>= 1.03 MPa	>= 150 psi	ASTM D412
Elongation at Break	>= 100 %	>= 100 %	ASTM D412
Tear Strength	6.13 kN/m	35.0 pli	ASTM D624
Compression Set	<= 60 % @Temperature 100 °C, Time 2.52e+6 sec	<= 60 % @Temperature 212 °F, Time 700 hour	ASTM D395, Method B

Thermal Properties	Metric	English	Comments
Thermal Conductivity	0.900 W/m-K @Pressure 2.07 MPa	6.25 BTU-in/hr-ft²-°F @Pressure 300 psi	ASTM D5470
Maximum Service Temperature, Air	150 °C	302 °F
Minimum Service Temperature, Air	-45.0 °C	-49.0 °F	Flex TR10; ASTM D1329
Flammability, UL94	V-0	V-0

Electrical Properties	Metric	English	Comments
Volume Resistivity	0.10 ohm-cm	0.10 ohm-cm	CEPS-0002
Shielding Effectiveness	>= 95 dB @Frequency 2.00e+9 Hz	>= 95 dB @Frequency 2.00e+9 Hz	Plane Wave; CHO-TM-TP08
	>= 95 dB @Frequency 1.00e+10 Hz	>= 95 dB @Frequency 1.00e+10 Hz	Plane Wave; CHO-TM-TP08
	>= 100 dB @Frequency 1.00e+8 Hz	>= 100 dB @Frequency 1.00e+8 Hz	E Field; CHO-TM-TP08
	>= 100 dB @Frequency 5.00e+8 Hz	>= 100 dB @Frequency 5.00e+8 Hz	E Field; CHO-TM-TP08

Descriptive Properties	Value	Comments
Binder	Silicone
Filler	Ni/C
Heat Aging	<0.25 ohm-cm	150°C for 48 hrs.