PTS PBT-6630 30% Glass Filled

Category	Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
Manufacturer	Polymer Technology & Services, LLC (PTS)
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PTS PBT-6630 30% Glass Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

PBT6630 is an injection molding grade, with 30% glass fiber reinforced, high heat stability, and electrical properties, easy to process. It is widely used in automotive, home appliance, Electrical industry, such as connector, gear housing, and other structural parts.Information provided by PTS LLC.

Physical Properties	Metric	English	Comments
Specific Gravity	1.53 g/cc	1.53 g/cc	ISO 1183
Melt Flow	13 g/10 min @Load 2.16 kg, Temperature 250 °C	13 g/10 min @Load 4.76 lb, Temperature 482 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	123 MPa	17800 psi	ISO 527-2/1
Elongation at Break	3.1 %	3.1 %	ISO 527-2/1
Tensile Modulus	9.01 GPa	1310 ksi	ISO 527-2/1A
Flexural Strength	189 MPa	27400 psi	ISO 178
Flexural Modulus	9.25 GPa	1340 ksi	ISO 178
Izod Impact, Notched (ISO)	7.50 kJ/m²	3.57 ft-lb/in²	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	202 °C	396 °F	ISO 75-1/-2
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in

Processing Properties	Metric	English
Nozzle Temperature	240 - 260 °C	464 - 500 °F
Melt Temperature	230 - 260 °C	446 - 500 °F
Mold Temperature	60.0 - 90.0 °C	140 - 194 °F
Drying Temperature	120 - 140 °C	248 - 284 °F
Dry Time	3 - 4 hour	3 - 4 hour
Back Pressure	0.300 - 0.700 MPa	43.5 - 102 psi

Descriptive Properties	Value	Comments
Processing Screw Speed	Medium-Fast