ExxonMobil Escorene® LL-3001 LLDPE/Hexene Premium Film Resin, Tough, 1.2 mil Film (discontinued **)

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Hexene, Film Grade
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Escorene® LL-3001 LLDPE/Hexene Premium Film Resin, Tough, 1.2 mil Film (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Data provided by the manufacturer, Exxon Chemical.A hexene copolymer LLDPE film resin. Films made from LL-3001 have outstanding tensile and toughness properties. The superior strength properties along with excellent drawability make this a very versatile packaging film resin. It is available with blown film additive formulations with or without slip and antiblock. A heavily stabilized formulation for cast film processing is also available.Applications: Stretch wrap; Stretch film; Frozen food packaging; Ice bags; Shipping sacks; Premium trash bags. Data for film properties below based on 1.2 mil film.

Physical Properties	Metric	English	Comments
Density	0.917 g/cc	0.0331 lb/in³	Exxon Method
Thickness	30.5 microns	1.20 mil
Melt Flow	1.0 g/10 min	1.0 g/10 min	Exxon Method

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	9.65 MPa	1400 psi	ASTM D882
Film Tensile Strength at Yield, TD	10.3 MPa	1490 psi	ASTM D882
Film Elongation at Break, MD	660 %	660 %	ASTM D882
Film Elongation at Break, TD	720 %	720 %	ASTM D882
Secant Modulus, MD	0.221 GPa	32.1 ksi	ASTM D882
Secant Modulus, TD	0.234 GPa	33.9 ksi	ASTM D882
Elmendorf Tear Strength MD	430 g	430 g	ASTM D1922
Elmendorf Tear Strength TD	740 g	740 g	ASTM D1922
Elmendorf Tear Strength, MD	14.1 g/micron	358 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	24.3 g/micron	617 g/mil	ASTM D1922
Dart Drop	8.19 g/micron	208 g/mil	F50; ASTM D1709
Dart Drop Test	250 g	0.551 lb	F50; ASTM D-1709
Film Tensile Strength at Break, MD	52.6 MPa	7630 psi	ASTM D882
Film Tensile Strength at Break, TD	42.6 MPa	6180 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	125 °C	257 °F	Exxon Method

Optical Properties	Metric	English	Comments
Haze	16 %	16 %	ASTM D1003
Gloss	50 %	50 %	45°, ASTM D-2457