PEAK Werkstoff DISPAL S542 Aluminum Alloy, AlMg6Mn4SiTiZrCo, Condition F

Category Metal , Nonferrous Metal , Aluminum Alloy
Manufacturer PEAK Werkstoff
Trade Name DISPAL
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PEAK Werkstoff DISPAL S542 Aluminum Alloy, AlMg6Mn4SiTiZrCo, Condition F.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by PEAK Werkstoff GmbH
Physical Properties Metric English Comments
Density 2.593 - 2.866 g/cc
0.09370 - 0.1036 lb/in³
Mechanical Properties Metric English Comments
Hardness, Vickers >= 130
>= 130
HV30
Tensile Strength at Break >= 85.0 MPa

@Temperature 300 °C
 >= 12300 psi

@Temperature 572 °F
>= 155 MPa

@Temperature 250 °C
 >= 22500 psi

@Temperature 482 °F
>= 230 MPa

@Temperature 200 °C
 >= 33400 psi

@Temperature 392 °F
>= 308 MPa

@Temperature 150 °C
 >= 44700 psi

@Temperature 302 °F
>= 422 MPa

@Temperature 100 °C
 >= 61200 psi

@Temperature 212 °F
>= 435 MPa

@Temperature 20.0 °C
 >= 63100 psi

@Temperature 68.0 °F
Tensile Strength, Yield >= 50.0 MPa

@Temperature 300 °C
 >= 7250 psi

@Temperature 572 °F
>= 110 MPa

@Temperature 250 °C
 >= 16000 psi

@Temperature 482 °F
>= 193 MPa

@Temperature 200 °C
 >= 28000 psi

@Temperature 392 °F
>= 252 MPa

@Temperature 150 °C
 >= 36500 psi

@Temperature 302 °F
>= 295 MPa

@Temperature 100 °C
 >= 42800 psi

@Temperature 212 °F
>= 300 MPa

@Temperature 20.0 °C
 >= 43500 psi

@Temperature 68.0 °F
Elongation at Break >= 6.5 %

@Temperature 20.0 °C
 >= 6.5 %

@Temperature 68.0 °F
>= 11 %

@Temperature 100 °C
 >= 11 %

@Temperature 212 °F
>= 31 %

@Temperature 200 °C
 >= 31 %

@Temperature 392 °F
>= 34 %

@Temperature 150 °C
 >= 34 %

@Temperature 302 °F
>= 45 %

@Temperature 250 °C
 >= 45 %

@Temperature 482 °F
>= 45 %

@Temperature 300 °C
 >= 45 %

@Temperature 572 °F
Modulus of Elasticity >= 47.0 GPa

@Temperature 300 °C
 >= 6820 ksi

@Temperature 572 °F
>= 54.0 GPa

@Temperature 250 °C
 >= 7830 ksi

@Temperature 482 °F
>= 60.0 GPa

@Temperature 200 °C
 >= 8700 ksi

@Temperature 392 °F
>= 66.0 GPa

@Temperature 150 °C
 >= 9570 ksi

@Temperature 302 °F
>= 71.0 GPa

@Temperature 100 °C
 >= 10300 ksi

@Temperature 212 °F
>= 77.0 GPa

@Temperature 20.0 °C
 >= 11200 ksi

@Temperature 68.0 °F
Poissons Ratio 0.311

@Temperature 20.0 °C
 0.311

@Temperature 68.0 °F
0.317

@Temperature 100 °C
 0.317

@Temperature 212 °F
0.321

@Temperature 150 °C
 0.321

@Temperature 302 °F
0.322

@Temperature 200 °C
 0.322

@Temperature 392 °F
0.329

@Temperature 250 °C
 0.329

@Temperature 482 °F
0.334

@Temperature 300 °C
 0.334

@Temperature 572 °F
Fatigue Strength 298.5 MPa
43290 psi
P50% rotary bending values for 5X10<sup>7</sup> cycles
Shear Modulus 24.0 GPa

@Temperature 300 °C
 3480 ksi

@Temperature 572 °F
25.0 GPa

@Temperature 250 °C
 3630 ksi

@Temperature 482 °F
27.0 GPa

@Temperature 200 °C
 3920 ksi

@Temperature 392 °F
28.0 GPa

@Temperature 150 °C
 4060 ksi

@Temperature 302 °F
29.0 GPa

@Temperature 100 °C
 4210 ksi

@Temperature 212 °F
31.0 GPa

@Temperature 20.0 °C
 4500 ksi

@Temperature 68.0 °F
Thermal Properties Metric English Comments
CTE, linear 21.8 - 22.8 µm/m-°C

@Temperature 20.0 - 100 °C
 12.1 - 12.7 µin/in-°F

@Temperature 68.0 - 212 °F
22.7 - 23.7 µm/m-°C

@Temperature 20.0 - 200 °C
 12.6 - 13.2 µin/in-°F

@Temperature 68.0 - 392 °F
23.6 - 24.6 µm/m-°C

@Temperature 20.0 - 300 °C
 13.1 - 13.7 µin/in-°F

@Temperature 68.0 - 572 °F
Melting Point 570 - 789 °C
1060 - 1450 °F
Solidus 570.3 - 576.3 °C
1059 - 1069 °F
Liquidus 783.1 - 789.1 °C
1442 - 1452 °F
Component Elements Properties Metric English Comments
Aluminum, Al 86 %
86 %
As Balance
Cobalt, Co 1.0 %
1.0 %
Magnesium, Mg 6.0 %
6.0 %
Manganese, Mn 4.0 %
4.0 %
Silicon, Si 1.0 %
1.0 %
Titanium, Ti 1.0 %
1.0 %
Zirconium, Zr 1.0 %
1.0 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.00000900 - 0.00000990 ohm-cm
0.00000900 - 0.00000990 ohm-cm