Manifattura Cattaneo PE UMW Polyethylene
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), UHMW PE Ultra High Molecular Weight |
| Manufacturer | Manifattura Cattaneo spa |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Manifattura Cattaneo PE UMW Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.020 % @Temperature 23.0 °C |
0.020 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | 0.20 % | 0.20 % | ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 63 | 63 | DIN 53505 |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | ISO 527 |
| Elongation at Break | >= 50 % | >= 50 % | ISO 527 |
| Elongation at Yield | 15 % | 15 % | ISO 527 |
| Tensile Modulus | 0.900 GPa | 131 ksi | ISO 527 |
| Compressive Yield Strength | 6.00 MPa @Strain 1.00 % |
870 psi @Strain 1.00 % |
ISO 604 |
| Poissons Ratio | 0.42 | 0.42 | |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 9.00 J/cm² | 42.8 ft-lb/in² | ISO 179 |
| Coefficient of Friction, Dynamic | 0.25 | 0.25 | on polished steel; MPC Test |
| Coefficient of Friction, Static | 0.16 | 0.16 | on polished steel; MPC Test |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 180 µm/m-°C | 100 µin/in-°F | ASTM D696 |
| Thermal Conductivity | 0.400 W/m-K | 2.78 BTU-in/hr-ft²-°F | DOM 52612 |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | ISO 75 |
| Vicat Softening Point | 80.0 °C | 176 °F | ISO 306 |
| Minimum Service Temperature, Air | -150 °C | -238 °F | |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+18 ohm-cm | >= 1.00e+18 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | IEC 60094 |
| Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 45.0 kV/mm @Thickness 2.00 mm |
1140 kV/in @Thickness 0.0787 in |
IEC 60243 |
| Dielectric Loss Index | 0.0010 @Frequency 1.00e+6 Hz |
0.0010 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Compliance Properties | Metric | English | Comments |
|---|---|---|---|
| FDA | Yes | Yes |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black | |
| Green | ||
| White | ||
| UV Resistance | N |
Users viewing this material also viewed the following:
- Polimeri Europa Riblene® FL 34 E Low Density Polyethylene - Blown Film Extrusion
- PSM Industries PolyAlloys MIM-14-4PH Heat Treated Stainless Steel
- Fainplast Compounds RKS 205/K-UV Rigid PVC, Antishock Extrusion Lead Free
- Imerys ImerPlastâ„¢ 10WPC Recycled Polyolefin Resin
- Saint-Gobain Norton® T-200 Mechanical Grade PTFE Sheet (0.250" thick)
- DuPont™ Bynel® 41E871 Anhydride Modified LLDPE
- Crucible Steel HALCOMB® 218 Tool Steel, AISI H11
- Ascend Performance Materials Vydyne® 66Z Nylon 66, Conditioned
- SABIC Innovative Plastics NORYL FN150 PPE+HIPS (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved