Oxford Polymers C-Acetal -30GF-Natural Acetal Copolymer, 30% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 30% Glass Fiber Reinforced
Manufacturer Oxford Polymers
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Oxford Polymers C-Acetal -30GF-Natural Acetal Copolymer, 30% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: Glass Fiber (30% Reinforced), Co-polymer Acetal, Injection Molding Grade Processing and Delivery Form: Pellets and Injection MoldingAdditives: Glass FiberSpecial Characteristics: Excellent creep resistanceInformation provided by Oxford Polymers
Physical Properties Metric English Comments
Density 1.58 g/cc
0.0571 lb/in³
ASTM D792
Water Absorption at Saturation 0.450 %
0.450 %
ASTM D570
Linear Mold Shrinkage, Flow 0.00400 cm/cm

@Thickness 3.17 mm
0.00400 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 125 MPa
18200 psi
ASTM D638
Elongation at Break 1.50 %
1.50 %
ASTM D638
Flexural Modulus 7.24 GPa
1050 ksi
ASTM D790
Izod Impact, Notched 0.854 J/cm

@Thickness 3.17 mm
1.60 ft-lb/in

@Thickness 0.125 in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 76.7 °C
170 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 177 - 199 °C
350 - 390 °F
Middle Barrel Temperature 182 - 204 °C
360 - 400 °F
Front Barrel Temperature 188 - 210 °C
370 - 410 °F
Nozzle Temperature 188 - 210 °C
370 - 410 °F
Melt Temperature 182 - 218 °C
360 - 425 °F
Mold Temperature 79.4 - 107 °C
175 - 225 °F
Drying Temperature 93.3 °C
200 °F
Dry Time 2.00 hour
2.00 hour