Outokumpu 4311 Cr-Ni Austenitic Stainless Steel

Category Metal , Ferrous Metal , Austenitic , Stainless Steel
Manufacturer Outokumpu
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Outokumpu 4311 Cr-Ni Austenitic Stainless Steel.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto), hot rolled strip/sheet (CPP), cold rolled strip/sheet, cold rolled narrow strip, bar, and rod forms.
Physical Properties Metric English Comments
Density 7.90 g/cc
0.285 lb/in³
RT
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate >= 550 MPa
>= 79800 psi
EN 10002-1
640 MPa
92800 psi
Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1
410 MPa

@Temperature 300 °C
 59500 psi

@Temperature 572 °F
 EN min.; EN 10002-5
430 MPa

@Temperature 200 °C
 62400 psi

@Temperature 392 °F
 EN min.; EN 10002-5
490 MPa

@Temperature 100 °C
 71100 psi

@Temperature 212 °F
 EN min.; EN 10002-5
850 MPa

@Temperature -80.0 °C
 123000 psi

@Temperature -112 °F
 EN min; EN 10002-5
1250 MPa

@Temperature -196 °C
 181000 psi

@Temperature -321 °F
 EN min; EN 10002-5
Tensile Strength, Yield 270 MPa

@Strain 0.200 %
 39200 psi

@Strain 0.200 %
 EN min.,RT; EN 10002-1
310 MPa

@Strain 1.00 %
 45000 psi

@Strain 1.00 %
 EN min.,RT; EN 10002-1
320 MPa

@Strain 0.200 %
 46400 psi

@Strain 0.200 %
 Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1
360 MPa

@Strain 1.00 %
 52200 psi

@Strain 1.00 %
 Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1
119 MPa

@Strain 0.200 %,
Temperature 500 °C
 17300 psi

@Strain 0.200 %,
Temperature 932 °F
 EN min.; EN 10002-5
125 MPa

@Strain 0.200 %,
Temperature 400 °C
 18100 psi

@Strain 0.200 %,
Temperature 752 °F
 EN min.; EN 10002-5
136 MPa

@Strain 0.200 %,
Temperature 300 °C
 19700 psi

@Strain 0.200 %,
Temperature 572 °F
 EN min.; EN 10002-5
149 MPa

@Strain 1.00 %,
Temperature 500 °C
 21600 psi

@Strain 1.00 %,
Temperature 932 °F
 EN min.; EN 10002-5
156 MPa

@Strain 1.00 %,
Temperature 400 °C
 22600 psi

@Strain 1.00 %,
Temperature 752 °F
 EN min.; EN 10002-5
157 MPa

@Strain 0.200 %,
Temperature 200 °C
 22800 psi

@Strain 0.200 %,
Temperature 392 °F
 EN min.; EN 10002-5
167 MPa

@Strain 1.00 %,
Temperature 300 °C
 24200 psi

@Strain 1.00 %,
Temperature 572 °F
 EN min.; EN 10002-5
187 MPa

@Strain 1.00 %,
Temperature 200 °C
 27100 psi

@Strain 1.00 %,
Temperature 392 °F
 EN min.; EN 10002-5
205 MPa

@Strain 0.200 %,
Temperature 100 °C
 29700 psi

@Strain 0.200 %,
Temperature 212 °F
 EN min.; EN 10002-5
240 MPa

@Strain 1.00 %,
Temperature 100 °C
 34800 psi

@Strain 1.00 %,
Temperature 212 °F
 EN min.; EN 10002-5
350 MPa

@Strain 0.200 %,
Temperature -80.0 °C
 50800 psi

@Strain 0.200 %,
Temperature -112 °F
 EN min.; EN 10002-5
420 MPa

@Strain 1.00 %,
Temperature -80.0 °C
 60900 psi

@Strain 1.00 %,
Temperature -112 °F
 EN min.; EN 10002-5
550 MPa

@Strain 0.200 %,
Temperature -196 °C
 79800 psi

@Strain 0.200 %,
Temperature -321 °F
 EN min.; EN 10002-5
650 MPa

@Strain 1.00 %,
Temperature -196 °C
 94300 psi

@Strain 1.00 %,
Temperature -321 °F
 EN min.; EN 10002-5
Elongation at Break >= 40.0 %
>= 40.0 %
EN 10002-1
55 %
55 %
Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1
35 %

@Temperature -196 °C
 35 %

@Temperature -321 °F
 EN min
40 %

@Temperature -80.0 °C
 40 %

@Temperature -112 °F
 EN min
Modulus of Elasticity 200 GPa
29000 ksi
RT
165 GPa

@Temperature 500 °C
 23900 ksi

@Temperature 932 °F
172 GPa

@Temperature 400 °C
 24900 ksi

@Temperature 752 °F
179 GPa

@Temperature 300 °C
 26000 ksi

@Temperature 572 °F
186 GPa

@Temperature 200 °C
 27000 ksi

@Temperature 392 °F
194 GPa

@Temperature 100 °C
 28100 ksi

@Temperature 212 °F
Poissons Ratio 0.30
0.30
RT
Shear Modulus 77.0 GPa
11200 ksi
calculated
Impact Test >= 60.0 J
>= 44.3 ft-lb
Hot rolled plate/Cold rolled strip/sheet, 10x10mm test pieces; EN 10045-1
Thermal Properties Metric English Comments
CTE, linear 16.0 µm/m-°C

@Temperature 100 °C
 8.89 µin/in-°F

@Temperature 212 °F
16.5 µm/m-°C

@Temperature 200 °C
 9.17 µin/in-°F

@Temperature 392 °F
17.0 µm/m-°C

@Temperature 300 °C
 9.44 µin/in-°F

@Temperature 572 °F
17.5 µm/m-°C

@Temperature 400 °C
 9.72 µin/in-°F

@Temperature 752 °F
18.0 µm/m-°C

@Temperature 500 °C
 10.0 µin/in-°F

@Temperature 932 °F
Specific Heat Capacity 0.500 J/g-°C
0.120 BTU/lb-°F
RT
Thermal Conductivity 15.0 W/m-K
104 BTU-in/hr-ft²-°F
RT
20.0 W/m-K

@Temperature 400 °C
 139 BTU-in/hr-ft²-°F

@Temperature 752 °F
Component Elements Properties Metric English Comments
Carbon, C 0.020 %
0.020 %
Chromium, Cr 18.5 %
18.5 %
Iron, Fe 70.84 %
70.84 %
Nickel, Ni 10.5 %
10.5 %
Nitrogen, N 0.14 %
0.14 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000730 ohm-cm
0.0000730 ohm-cm
RT