Material Notes:

LNP* LUBRICOMP* ZFG26 is a compound based on PPE+PS resin containing 30% Glass Fiber, 10% Graphite. Added features of this material include: Wear Resistant.

Physical Properties	Metric	English	Comments
Density	1.37 g/cc	0.0495 lb/inÂ³	ISO 1183
	1.42 g/cc	0.0513 lb/inÂ³	ASTM D792
Moisture Absorption	0.0600 %	0.0600 %	50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow	0.0020 cm/cm @Time 86400 sec	0.0020 in/in @Time 24.0 hour	ASTM D955
	0.0036 cm/cm @Time 86400 sec	0.0036 in/in @Time 24.0 hour	ISO 294
Linear Mold Shrinkage, Transverse	0.0070 cm/cm @Time 86400 sec	0.0070 in/in @Time 24.0 hour	ASTM D955
	0.0073 cm/cm @Time 86400 sec	0.0073 in/in @Time 24.0 hour	ISO 294

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	109 MPa	15800 psi	ISO 527
	115 MPa	16700 psi	ASTM D638
Tensile Strength, Yield	109 MPa	15800 psi	ASTM D638
	109 MPa	15800 psi	ISO 527
Elongation at Break	1.5 %	1.5 %	ASTM D638
	1.5 %	1.5 %	ISO 527
Elongation at Yield	1.5 %	1.5 %	ASTM D638
	1.5 %	1.5 %	ISO 527
Tensile Modulus	10.48 GPa	1520 ksi	1 mm/min; ISO 527
	13.1 GPa	1900 ksi	50 mm/min; ASTM D638
Flexural Strength	163 MPa	23600 psi	ISO 178
	165 MPa	23900 psi	ASTM D790
Flexural Modulus	10.0 GPa	1450 ksi	ISO 178
	10.48 GPa	1520 ksi	ASTM D790
Izod Impact, Notched	0.800 J/cm	1.50 ft-lb/in	ASTM D256
Izod Impact, Unnotched	3.77 J/cm	7.06 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	8.00 kJ/mÂ²	3.81 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	28.0 kJ/mÂ²	13.3 ft-lb/inÂ²	80104; ISO 180/1U
Dart Drop, Total Energy	6.00 J	4.43 ft-lb	Instrumented Impact Energy @ peak; ASTM D3763
Impact Test	3.00 J	2.21 ft-lb	Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic	0.62	0.62	ASTM D3702 Modified
Coefficient of Friction, Static	0.89	0.89	ASTM D3702 Modified
K (wear) Factor	228 x 10^-8 mmÂ³/N-M	113 x 10^-10 inÂ³-min/ft-lb-hr	Washer; ASTM D3702 Modified

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	46.8 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	26.0 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	47.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	26.1 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
CTE, linear, Transverse to Flow	21.6 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	12.0 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	22.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	12.2 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	141 Â°C	286 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
	140 Â°C @Thickness 3.20 mm	284 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	135 Â°C	275 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	135 Â°C @Thickness 3.20 mm	275 Â°F @Thickness 0.126 in	unannealed; ASTM D648