Network Polymers Softflex® 9000
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber |
| Manufacturer | Network Polymers |
| Trade Name | Softflex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Network Polymers Softflex® 9000.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Softflex® Thermoplastic Elastomer AlloyInformation provided by Network Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0080 cm/cm @Thickness 3.17 mm |
0.0070 - 0.0080 in/in @Thickness 0.125 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0080 cm/cm @Thickness 3.17 mm |
0.0070 - 0.0080 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 3.4 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.4 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| 36 g/10 min @Load 1.00 kg, Temperature 235 °C |
36 g/10 min @Load 2.20 lb, Temperature 455 °F |
Procedure A Condition Q; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 87 - 97 | 87 - 97 | Instantaneous; ASTM D2240 |
| Hardness, Shore D | 65 | 65 | |
| Tensile Strength, Yield | 44.8 MPa | 6500 psi | chs 20 in/min; ASTM D412 |
| Elongation at Break | 450 % | 450 % | ASTM D412 |
| 50% Modulus | 0.00760 GPa | 1.10 ksi | ASTM D412 |
| 100% Modulus | 0.0112 GPa | 1.62 ksi | ASTM D412 |
| 300% Modulus | 0.0248 GPa | 3.60 ksi | ASTM D412 |
| Tear Strength | 133 kN/m | 759 pli | |
| Taber Abrasion, mg/1000 Cycles | 10 | 10 | H22 Wheel 1000 g load/1000 cycles; ASTM D3389 |
| Compression Set | 25 % | 25 % | Method B, 22 hours at 25% deflection and 23°C; ASTM D395 |
Users viewing this material also viewed the following:
- REXtac Rextac® RT 2732 Amorphous Polyalphaolefin (APAO)
- ExxonMobil Escorene® LD-141 EVA Shrink Film Resin, FMI (discontinued **)
- Magyar Aluminum ALO-Ex35 LS Alumina
- MarkeTech Yttrium-Stabilized Zirconia (YSZ) Single Crystal Substrate
- Kraton® D3158 DT-B (SBS) Compound
- Haynes Hastelloy® C-22® alloy, 30% cold worked sheet
- Dow DNDA-8335 NT 7 Linear Low Density Polyethylene Resin
- DuPont Performance Polymers Zytel® 103FHS BKB038 Nylon 66 (Unverified Data**)
- Fainplast Compounds PMP 77 Flexible PVC, Extrusion Modified with PU
Copyright © lookpolymers.com All Rights Reserved