Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber |
Manufacturer | Network Polymers |
Trade Name | Softflex® |
Port | Ningbo port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | Network Polymers Softflex® 0809.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 0.925 g/cc | 0.925 g/cc | ASTM D792 |
Linear Mold Shrinkage | 0.017 - 0.020 cm/cm @Thickness 3.17 mm |
0.017 - 0.020 in/in @Thickness 0.125 in |
ASTM D955 |
Melt Flow | 3.0 g/10 min @Load 1.00 kg, Temperature 235 °C |
3.0 g/10 min @Load 2.20 lb, Temperature 455 °F |
Procedure A Condition Q; ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Hardness, Shore A | 31 | 31 | 10 second dwell; ASTM D2240 |
36 | 36 | Instantaneous; ASTM D2240 | |
Tensile Strength, Yield | 4.54 MPa | 659 psi | chs 20 in/min; ASTM D412 |
Elongation at Break | 605 % | 605 % | ASTM D412 |
Gardner Impact | 137.1 J @Temperature -30.0 °C |
101.1 ft-lb @Temperature -22.0 °F |
ASTM D5420 |
Taber Abrasion, mg/1000 Cycles | 1.1797 | 1.1797 | H22 Wheel 1000 g load/1000 cycles; ASTM D3389 |
Compression Set | 19.9 % | 19.9 % | Method B, 22 hours at 25% deflection and 23°C; ASTM D395 |
76.2 % @Temperature 70.0 °C |
76.2 % @Temperature 158 °F |
22 hours at 25% deflection; ASTM D395, Method B, | |
82.4 % @Temperature 100 °C |
82.4 % @Temperature 212 °F |
22 hours at 25% deflection; ASTM D395, Method B, | |
Tensile Set | 4.9 % | 4.9 % | 100% strain; ASTM D412 |