Network Polymers PC-1029
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Network Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Network Polymers PC-1029.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Natural PolycarbonateInformation provided by Network Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | 24 hours at 73°F; ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 230 °C |
20 g/10 min @Load 4.76 lb, Temperature 446 °F |
Procedure A Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | chs 2 in/min; ASTM D638 |
| Flexural Strength | 89.6 MPa | 13000 psi | Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790 |
| Flexural Modulus | 2.38 GPa | 345 ksi | Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790 |
| Izod Impact, Notched | 6.41 J/cm | 12.0 ft-lb/in | Test Method A (0.125 in bar); ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | 0.125 in bar; ASTM D648 |
| Flammability, UL94 | V-2 | V-2 | 0.062 in, All Colors |
Users viewing this material also viewed the following:
- Plastcom SLOVASTER® B1 GF 20 000/2 PBT, 20% glass fibre
- Nye Lubricants 902B (NG) Synthetic Oil
- Albis Plastics Cellulose Acetate Butyrate B9024 (UVI, Odor Mask Added), 10% Plasticizer (discontinued **)
- SABIC Innovative Plastics LNP STAT-KON DE002ER PC
- Samsung Cheil Industries Starex® SG-501 Expandable Polystyrene (EPS) High Expansion
- Solvay STANNINE® 5525 Surfactant
- Master Bond EP21LV-LO Two Component, Lower Viscosity, Room Temperature Curing Epoxy System
- Carpenter Custom 455® Stainless Steel, Condition H900 (Age Hardened 482°C)
- Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 11.1 mm thick plate, aged 3 hours at 816°C
Copyright © lookpolymers.com All Rights Reserved