NYCOA 589 PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | NYCOA, Inc. |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NYCOA 589 PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FDA approved molding, extrusion and blown film gradeInformation provided by NYCOA, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Water Absorption | 1.7 % | 1.7 % | ASTM D570 |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ASTM D638 |
| Elongation at Break | >= 100 % | >= 100 % | ASTM D638 |
| Flexural Yield Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| Flexural Modulus | 2.455 GPa | 356.1 ksi | ASTM D790 |
| Izod Impact, Notched | 0.750 J/cm | 1.41 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | ASTM D789 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 250 °C | 482 °F | |
| Rear Barrel Temperature | 220 °C | 428 °F | |
| Middle Barrel Temperature | 230 °C | 446 °F | |
| Front Barrel Temperature | 250 °C | 482 °F | |
| Nozzle Temperature | 250 °C | 482 °F | |
| Mold Temperature | 80.0 °C | 176 °F | |
| Drying Temperature | 76.0 °C | 169 °F |
Users viewing this material also viewed the following:
- PolyOne Syncure™ S1006B Polyethylene, Crosslinked (XLPE)
- MetaFoam Copper Foam
- Huntsman IROGRAN® A 89 E 4372 Polyester-Based TPU-Injection Extrusion Grade
- SABIC Innovative Plastics LNP STAT-KON EE003XXC PEI
- DuPont Teijin Films Teijin® Tetoron® HS Polyester Film, 1000 Gauge
- 3M PN8029 Marine Grade Silicone Sealant
Copyright © lookpolymers.com All Rights Reserved