NYCOA 578 PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Extruded |
| Manufacturer | NYCOA, Inc. |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NYCOA 578 PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
very high viscosity molding & extrusion grade for tubing, pipes, film and tapesInformation provided by NYCOA, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Water Absorption | 1.7 % | 1.7 % | ASTM D570 |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ASTM D638 |
| Elongation at Break | >= 100 % | >= 100 % | ASTM D638 |
| Flexural Yield Strength | 92.0 MPa | 13300 psi | ASTM D790 |
| Flexural Modulus | 2.455 GPa | 356.1 ksi | ASTM D790 |
| Izod Impact, Notched | 0.750 J/cm | 1.41 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 117 °C | 243 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 250 °C | 482 °F | |
| Rear Barrel Temperature | 220 °C | 428 °F | |
| Middle Barrel Temperature | 230 °C | 446 °F | |
| Front Barrel Temperature | 250 °C | 482 °F | |
| Nozzle Temperature | 250 °C | 482 °F | |
| Mold Temperature | 80.0 °C | 176 °F | |
| Drying Temperature | 76.0 °C | 169 °F |
Users viewing this material also viewed the following:
- Ferro CF 1417 Low-Temperature Sealing
- Lucent Polymers PPC-320 Polypropylene, Impact Modified
- Sharadaa Ceramics ZAP 003 Smart Cast Application
- Techmer ES HiFill® PA6 GF44 HS X 44% Glass Filled
- SMAC CABLE® 2524S-20-08 Damping Material
- Chase Plastics CP Pryme® NN100STL (COND, 50% RH) Nylon 66, Super Toughened, Internally Lubricated
- A. Schulman POLYBATCH™ Grey 8760 Concentrate Based In Polyethylene
- Universal Wire Works 80SD-2 Steel Welding Wire
- Chosun Refractories A-7 Insulating Firebrick
- Axiall PURGOVIN® 8000 Rigid PVC, Extrusion
Copyright © lookpolymers.com All Rights Reserved