NOVA Chemicals Sclair® 16A Butene HDPE Film Resin (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Copolymer Film Grade |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Sclair® 16A Butene HDPE Film Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Film Properties. Features: Low gel, good barrier properties.Applications: Merchandising bags, lamination, co-extrusion.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.946 g/cc | 0.0342 lb/in³ | ASTM D792 |
| Moisture Vapor Transmission | 0.150 cc-mm/m²-24hr-atm | 0.381 cc-mil/100 in²-24hr-atm | ASTM D1434 |
| Water Vapor Transmission | 6.00 g/m²/day | 0.386 g/100 in²/day | ASTM D1434 |
| Oxygen Transmission | 55.0 cc-mm/m²-24hr-atm | 140 cc-mil/100 in²-24hr-atm | or 2200 cc/m²-atm-24 hr per 25 µm film; 38°C; 90% RH Difference |
| Melt Flow | 0.27 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.27 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 60 | 60 | ASTM D2240 |
| Film Tensile Strength at Yield, MD | 21.0 MPa | 3050 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 23.0 MPa | 3340 psi | ASTM D882 |
| Film Elongation at Break, MD | 600 % | 600 % | ASTM D882 |
| Film Elongation at Break, TD | 850 % | 850 % | ASTM D882 |
| Secant Modulus, MD | 0.590 GPa | 85.6 ksi | ASTM D882 |
| Secant Modulus, TD | 0.680 GPa | 98.6 ksi | ASTM D882 |
| Coefficient of Friction | 0.30 | 0.30 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 1.00 g/micron | 25.4 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 23.0 g/micron | 584 g/mil | ASTM D1922 |
| Dart Drop | 0.600 g/micron | 15.2 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 38.0 MPa | 5510 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 121 °C | 250 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 230 °C | 428 - 446 °F |
Users viewing this material also viewed the following:
- Renegade Materials Corporation RM-3006 Bismaleimide (BMI) Paste Adhesive
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with DBP
- LATI Latimass 82-06 D030 PA12
- Shamrock Technologies NanoFLON® P 47A Thermoplastic Grade PTFE Additive
- Polyram PlusTek PB825G5 Nylon 6, 25% Glass Fiber
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 60 PHR Carbon Black, N-220 (ISAF)
- ChevronTexaco Taro® 16 XD SAE 40
- Fainplast Compounds Hax™ CAT 103T Catalyst for Cable Compound
- Arlon 48576R006 0.0055" Uncured Silicone Rubber with Fiberglass Substrate
- DuPont Elvax® 3175 Ethylene-Vinyl Acetate Copolymer Resin for Coextrusion
Copyright © lookpolymers.com All Rights Reserved