NOVA Chemicals Sclair® 15A Butene HDPE Film Resin
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Copolymer Film Grade |
| Manufacturer | NOVA Chemicals |
| Trade Name | Sclair® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Sclair® 15A Butene HDPE Film Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Film Properties. Features: Low gel, good barrier properties, strength and toughness.Applications: Lamination, co-extrusion.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.942 g/cc | 0.0340 lb/in³ | ASTM D792 |
| Water Vapor Transmission | 5.40 g/m²/day | 0.348 g/100 in²/day | |
| Oxygen Transmission | 65.0 cc-mm/m²-24hr-atm | 165 cc-mil/100 in²-24hr-atm | or 2600 cc/m²-atm-24 hr per 25 µm film; 38°C; 90% RH Difference |
| Oxygen Transmission Rate | 2400 cc/m²/day | 155 cc/100 in²/day | ASTM D1434 |
| Thickness | 38.0 microns | 1.50 mil | |
| Melt Flow | 0.33 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.33 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 59 | 59 | ASTM D2240 |
| Film Tensile Strength at Yield, MD | 21.0 MPa | 3050 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 22.0 MPa | 3190 psi | ASTM D882 |
| Film Elongation at Break, MD | 430 % | 430 % | ASTM D882 |
| Film Elongation at Break, TD | 900 % | 900 % | ASTM D882 |
| Secant Modulus, MD | 0.510 GPa | 74.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.690 GPa | 100 ksi | ASTM D882 |
| Coefficient of Friction | 0.26 | 0.26 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 0.600 g/micron | 15.2 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 26.0 g/micron | 660 g/mil | ASTM D1922 |
| Dart Drop | 1.31 g/micron | 33.3 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 54.0 MPa | 7830 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 39.0 MPa | 5660 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 119 °C | 246 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 230 °C | 428 - 446 °F |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PH 51 T 40 Polypropylene Homopolymer, 40% Micronized Talc
- Hong Kun Group 3-Chloro-2-fluorobenzaldehyde Pharmaceutical Intermediate
- MarkeTech Repton 125 Aluminum Oxide
- SABIC Innovative Plastics ULTEM ATX3562R PEI+PCE (Asia Pacific)
- Shakespeare WonderThread® SN-40 ultra soft TEX# 50 Nylon Industrial Sewing Thread
- A. Schulman FORMION™ FI 372 Ionomer
- Destech Silicon Carbide, Solid or Foamed
- Epoxy Technology EPO-TEK® B912-8 Epoxy
- Fainplast Compounds FR 70/1 Flexible PVC, Insulation
- Diamond Polymers NYLON 6650HSL Black
Copyright © lookpolymers.com All Rights Reserved