Aaron Industries AAROLENE® ARPP C 200-2 Polypropylene Compounded Resin
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Aaron Industries Corporation |
| Trade Name | AAROLENE® ARPP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aaron Industries AAROLENE® ARPP C 200-2 Polypropylene Compounded Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
AAROLENE® ARPP 200 Series Polypropylene Compounded ResinColor may be specified. Melt Flow Index may be specified.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.022 cm/cm | 0.022 in/in | ASTM D955 |
| Melt Flow | 4.0 - 30 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 - 30 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 35.2 MPa | 5100 psi | ASTM D638 |
| Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm | 2.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 128 °C | 262 °F | ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 221R PC (Asia Pacific)
- Lushan H-4 Adhesive Resin for Aluminum Plastic Composite Pipe
- A. Schulman POLYFLAM™ FPP 1006 Talc Filled Homopolymer Polypropylene
- Total HDPE 56020 S High Density Polyethylene - Blow Molding
- Toyobo Vylopet® EMC245K Glass Reinforced Polyester, Easy Molding Grade
- Daikin NEOFLON RP-5000AS EFEP Pellets
- BASF Ultramid® 8270 HS BK 102 PA6 (Dry)
- ATI Allegheny Ludlum Grade 18 Titanium (UNS R56322)
- BASF Sicotan® Yellow L 1910 Color Additive
- 3M Scotch-Weld™ 1870 Industrial Adhesive
Copyright © lookpolymers.com All Rights Reserved