NOVA Chemicals Sclair® 12J1 Octene LLDPE Film Resin (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Octene, Film |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Sclair® 12J1 Octene LLDPE Film Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Film Properties. Features: Low gel, high clarity.Applications: Overwrap, lamination.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ASTM D792 |
| Moisture Vapor Transmission | 0.350 cc-mm/m²-24hr-atm | 0.889 cc-mil/100 in²-24hr-atm | ASTM D1434 |
| Water Vapor Transmission | 14.0 g/m²/day | 0.902 g/100 in²/day | ASTM D1434 |
| Melt Flow | 0.95 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.95 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 58 | 58 | ASTM D2240 |
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 12.0 MPa | 1740 psi | ASTM D882 |
| Film Elongation at Break, MD | 720 % | 720 % | ASTM D882 |
| Film Elongation at Break, TD | 940 % | 940 % | ASTM D882 |
| Secant Modulus, MD | 0.218 GPa | 31.6 ksi | ASTM D882 |
| Secant Modulus, TD | 0.243 GPa | 35.2 ksi | ASTM D882 |
| Coefficient of Friction | >= 0.40 | >= 0.40 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 10.0 g/micron | 254 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 22.0 g/micron | 559 g/mil | ASTM D1922 |
| Dart Drop | 5.00 g/micron | 127 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 43.0 MPa | 6240 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 37.0 MPa | 5370 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 110 °C | 230 °F | ASTM D1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D696 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 8.0 % @Thickness 0.0250 mm |
8.0 % @Thickness 0.000984 in |
ASTM D1003 |
| Gloss | 63 % | 63 % | 45°; 1 mil; ASTM D1894 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 210 - 220 °C | 410 - 428 °F |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers Amodel® AF-1550 V0 Polyphthalamide (PPA) Resin, 50% Glass/Mineral Reinforced, Dry As Molded &
- Lotte Chemical Titan TITANEX® LF2021 Linear low density polyethylene resin (discontinued **)
- Eastman 1840F Polyethylene (discontinued **)
- NOVA Chemicals Dylark® 378P12 Glass Reinforced Engineering Resin
- Mid-Mountain Materials ARMATEX® FF18 Fluoroelastomer Coated Glass Fabric
- Solvay Specialty Polymers Tecnoflon® PL 458 Fluoroelastomer
- Sumitomo Chemical Sumipex® LG Acrylic Resin, High Flow
- Toyobo VYLOPET® EMC545 Injection Molding Polyester Resin, Glass Reinforced
- Chosun Refractories SCX-60KL Special SiC Castable
Copyright © lookpolymers.com All Rights Reserved