NOVA Chemicals Sclair® 11H1 LLDPE Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Sclair® 11H1 LLDPE Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Low gel, Excellent heat sealability, Easy processability, High toughness and strengthApplications: Heavy duty sack, High strength packagingAdditives: Process stabilizer, Polymer process aid, AntiblockCanada: The Health Protection Branch has indicated no objection to the sue in Canada of this resin for a variety of food packaging applications. Information on the packaging of specific foodstuffs should obtained from NOVA Chemicals or from the Health Protection Branch, Food Packaging Materials and Incidental Additives Section, Ottawa, Canada.United States: This resin complies with the specification contained in the U.S. Food and Drug Administration (FDA) regulation 21 CFR 177.1520 for olefin polymer, para. (c) 3.2a, and may thus be used in the United States as an article or component of an article intended for use in contact with food.Film properties are typical of blown film extruded at a blowup ratio of 2.5:1, but are dependent upon operating conditions.Information provided by NOVA Chemicals.
Physical Properties Metric English Comments
Density 0.920 g/cc
0.0332 lb/in³
ASTM D792
Thickness 25.0 - 75.0 microns
0.984 - 2.95 mil
Melt Flow 0.80 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.80 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 9.50 MPa
1380 psi
ASTM D882
Film Tensile Strength at Yield, TD 10.0 MPa
1450 psi
ASTM D882
Film Elongation at Break, MD 640 %
640 %
ASTM D882
Film Elongation at Break, TD 770 %
770 %
ASTM D882
Secant Modulus, MD 0.190 GPa
27.6 ksi
at 1%; ASTM D882
Secant Modulus, TD 0.200 GPa
29.0 ksi
at 1%; ASTM D882
Impact 48
48
J/mm; NOVA Chemicals Puncture test
Coefficient of Friction 0.60
0.60
ASTM D1894
Elmendorf Tear Strength, MD 20.0 g/micron
508 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 24.0 g/micron
610 g/mil
ASTM D1922
Dart Drop 7.00 g/micron
178 g/mil
F<sub>50</sub>, ASTM D1709/A
Film Tensile Strength at Break, MD 41.3 MPa
5990 psi
ASTM D882
Film Tensile Strength at Break, TD 40.7 MPa
5900 psi
ASTM D882
Optical Properties Metric English Comments
Haze 12 %
12 %
1 mil; ASTM D1003
Gloss 50 %
50 %
at 45°; 1 mil; ASTM D2457
Processing Properties Metric English Comments
Melt Temperature 220 - 230 °C
428 - 446 °F
Die Opening 0.0900 - 0.220 cm
0.0354 - 0.0866 in
Descriptive Properties Value Comments
Blow Up Ratio 2:1 to 3:1