NOVA Chemicals Novapol® TF-Y822-CP Hexene LLDPE Film Resin

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Hexene, Film Grade
Manufacturer	NOVA Chemicals
Trade Name	Novapol®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	NOVA Chemicals Novapol® TF-Y822-CP Hexene LLDPE Film Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Film Properties. Features: Good stiffness and machinability, exceptional toughness, suitable for narrow die gaps.Applications: Heavy duty sacks, high strength packaging.Data provided by the manufacturer.

Physical Properties	Metric	English	Comments
Density	0.921 g/cc	0.0333 lb/in³	ASTM D792
Thickness	38.1 microns	1.50 mil
Melt Flow	0.80 g/10 min @Load 2.16 kg, Temperature 190 °C	0.80 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	10.0 MPa	1450 psi	ASTM D882
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	ASTM D882
Film Elongation at Break, MD	650 %	650 %	ASTM D882
Film Elongation at Break, TD	850 %	850 %	ASTM D882
Secant Modulus, MD	0.180 GPa	26.1 ksi	ASTM D882
Secant Modulus, TD	0.200 GPa	29.0 ksi	ASTM D882
Coefficient of Friction	>= 0.50	>= 0.50	ASTM D1894
Elmendorf Tear Strength, MD	13.0 g/micron	330 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	22.8 g/micron	579 g/mil	ASTM D1922
Dart Drop	6.30 g/micron	160 g/mil	F 50; ASTM D1709/A
Film Tensile Strength at Break, MD	32.0 MPa	4640 psi	ASTM D882
Film Tensile Strength at Break, TD	28.0 MPa	4060 psi	ASTM D882

Optical Properties	Metric	English	Comments
Haze	10 % @Thickness 0.0250 mm	10 % @Thickness 0.000984 in	ASTM D1003
Gloss	60 %	60 %	45°; 1 mil; ASTM D1894

Processing Properties	Metric	English	Comments
Melt Temperature	195 - 220 °C	383 - 428 °F