- NOVA Chemicals Novapol® TF-Y822-BP Hexene LLDPE Film Resin
NOVA Chemicals Novapol® TF-Y822-BP Hexene LLDPE Film Resin
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Hexene, Film Grade |
| Manufacturer | NOVA Chemicals |
| Trade Name | Novapol® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Novapol® TF-Y822-BP Hexene LLDPE Film Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Film Properties. Features: Good stiffness and machinability, exceptional toughness.Applications: Industrial packaging, high strength liners.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ASTM D792 |
| Thickness | 38.1 microns | 1.50 mil | |
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.80 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Elongation at Break, MD | 650 % | 650 % | ASTM D882 |
| Film Elongation at Break, TD | 850 % | 850 % | ASTM D882 |
| Secant Modulus, MD | 0.180 GPa | 26.1 ksi | ASTM D882 |
| Secant Modulus, TD | 0.200 GPa | 29.0 ksi | ASTM D882 |
| Coefficient of Friction | <= 0.25 | <= 0.25 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 13.0 g/micron | 330 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 22.8 g/micron | 579 g/mil | ASTM D1922 |
| Dart Drop | 6.30 g/micron | 160 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 32.0 MPa | 4640 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 28.0 MPa | 4060 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 10 % @Thickness 0.0250 mm |
10 % @Thickness 0.000984 in |
ASTM D1003 |
| Gloss | 60 % | 60 % | 45°; 1 mil; ASTM D1894 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 195 - 220 °C | 383 - 428 °F |
Users viewing this material also viewed the following:
- Nabaltec APYRAL® 22 Al(OH)3
- LATI LARPEEK 50 G/40 40% Glass Reinforced Polyetheretherketone (PEEK) (discontinued **)
- SABIC Innovative Plastics LNP LUBRICOMP KZL16 Acetal Copolymer
- SolVin 260RF Polyvinyl Chloride General Purpose - Rigid
- Master Bond MasterSil 709 One Part Silicone Meets MIL Spec
- A. Schulman POLYFORT™ FPP 3711 High Impact Polypropylene
- Diamond Polymers ABS 3500 EF-Low Gel Extrusion Grade, Low Gel
- Ashley Polymers Ashlene® 528L-50G Nylon 66, 50% Glass Reinforced
- Atom Adhesives AA-DUCT N02 Epoxy Adhesive
- Pau Tai UNISTAB BZ-591 Liquid Barium-Zinc Stabilizer
Copyright © lookpolymers.com All Rights Reserved