NOVA Chemicals Novapol® GF-0218-F Butene LLDPE Masterbatch Resin
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Compounding Resin |
| Manufacturer | NOVA Chemicals |
| Trade Name | Novapol® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Novapol® GF-0218-F Butene LLDPE Masterbatch Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Film Properties. Features: Free flowing granules, toughness and strength, ease of extrusion.Applications: Blending, concentrates.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D792 |
| Thickness | 38.1 microns | 1.50 mil | |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 9.00 MPa | 1310 psi | ASTM D882 |
| Film Elongation at Break, MD | 690 % | 690 % | ASTM D882 |
| Film Elongation at Break, TD | 740 % | 740 % | ASTM D882 |
| Secant Modulus, MD | 0.180 GPa | 26.1 ksi | ASTM D882 |
| Secant Modulus, TD | 0.200 GPa | 29.0 ksi | ASTM D882 |
| Coefficient of Friction | >= 0.70 | >= 0.70 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 3.50 g/micron | 88.9 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 10.6 g/micron | 269 g/mil | ASTM D1922 |
| Dart Drop | 3.00 g/micron | 76.2 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 14 % @Thickness 0.0250 mm |
14 % @Thickness 0.000984 in |
ASTM D1003 |
| Gloss | 50 % | 50 % | 45°; 1 mil; ASTM D1894 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 195 - 220 °C | 383 - 428 °F |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 NG1 GF 20 HLS PA6, 20% glass fibre, combined stability
- Radici Radilon® A ECP3808 (dry) Nylon 66
- SABIC Innovative Plastics Lexan® 141R PC (Europe-Africa-Middle East)
- Gouda Vuurvast ADHESIET 160 SP Dry Air-Setting Refractory Mortar
- Lord Adhesives 7713 Adhesion Increaser to SMC
- LTL Color Compounds ColorFast® FRPBT210 PBT, Flame Retarded, Impact Modified
- Total FE 8000 LDPE blown film
- ATG s.r.l. FVMQ Fluorosilicone Rubber
- Hexion Bakelite™ PF 4155 Phenolic Formaldehyde Resin, Resistant to High Temperatures, Improved Electrical Properties, Low Shrinkage, High Mechanical Strength
Copyright © lookpolymers.com All Rights Reserved