- NIZHNEKAMSKNEFTEKHIM PE 4122N (22401) Linear Low Density Polyethylene
NIZHNEKAMSKNEFTEKHIM PE 4122N (22401) Linear Low Density Polyethylene
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LLDPE |
| Manufacturer | NIZHNEKAMSKNEFTEKHIM Inc |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NIZHNEKAMSKNEFTEKHIM PE 4122N (22401) Linear Low Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 - 0.924 g/cc | 0.0332 - 0.0334 lb/in³ | Base Resin; ASTM D1505 |
| Melt Flow | 0.90 - 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.90 - 1.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1283/L |
| 27 - 39 g/10 min @Load 21.6 kg, Temperature 190 °C |
27 - 39 g/10 min @Load 47.6 lb, Temperature 374 °F |
Flow@21.6kg/Flow@2.16kg ratio < 30; ASTM D1283 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | >= 45.0 MPa | >= 6530 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | >= 30.0 MPa | >= 4350 psi | ASTM D882 |
| Film Elongation at Break, MD | >= 650 % | >= 650 % | ASTM D882 |
| Film Elongation at Break, TD | >= 700 % | >= 700 % | ASTM D882 |
| Tensile Modulus | >= 0.150 GPa | >= 21.8 ksi | 2% sec, MD; ASTM D882 |
| >= 0.180 GPa | >= 26.1 ksi | 2% sec, TD; ASTM D882 | |
| Elmendorf Tear Strength, MD | >= 4.72 g/micron | >= 120 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | >= 15.7 g/micron | >= 400 g/mil | ASTM 1922 |
| Dart Drop Test | >= 80.0 g | >= 0.176 lb | ASTM D1709 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Gel Content (pcs./m²) | 0 | > 1mm |
| 245 | (0.2-0.5)mm | |
| 250 | > 0.2mm (totally) | |
| 5 | (0.5-1.0)mm |
Users viewing this material also viewed the following:
- Polimeri Europa Riblene® FF 33 Low Density Polyethylene - Blown Film Extrusion
- ND Industries 541 Shaft & Bearing Retainer Retaining Compound
- SABIC Innovative Plastics Lexan® 4704 PPC
- 3M Dyneon™ Fluorel™ FC-2123 Fluoroelastomer VF2 + HFP Dipolymer (discontinued **)
- LG Chemical Lupox® PBT-LW5303F 30% Glass Filled Low Warp Flame Retardant PBT
- Momentive Performance Materials RTV133 Black Adhesive Sealant, Flame Retardant Paste
- SABIC Innovative Plastics NORYL REN501 PPE+PS
- Styron Pulse® 920 MG PC/ABS
- Eagle Brass 110 EPT COPPER, 3/4 Hard
- LG Chemical SG175G ABS, Super Surface Gloss, High Flow
Copyright © lookpolymers.com All Rights Reserved