- Kennametal Stellite Stellite® 31 PM cast aged 8 hours at 802°C air cooled
Kennametal Stellite Stellite® 31 PM cast aged 8 hours at 802°C air cooled
| Category | Metal , Nonferrous Metal , Cobalt Alloy , Superalloy |
| Manufacturer | Kennametal Stellite |
| Trade Name | Stellite® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kennametal Stellite Stellite® 31 PM cast aged 8 hours at 802°C air cooled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous wear parts. Data provided by the manufacturer, Deloro Stellite Inc.Product of former Deloro Stellite Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.45 g/cc | 0.305 lb/in³ | P/M (98%) |
| 8.61 g/cc | 0.311 lb/in³ | Theoretical |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 842 MPa | 122000 psi | |
| Tensile Strength, Yield | 662 MPa @Strain 0.200 % |
96000 psi @Strain 0.200 % |
|
| Elongation at Break | 2.0 % | 2.0 % | in 25.4 mm |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 14.1 µm/m-°C @Temperature 21.0 - 316 °C |
7.83 µin/in-°F @Temperature 69.8 - 601 °F |
|
| 14.5 µm/m-°C @Temperature 21.0 - 427 °C |
8.06 µin/in-°F @Temperature 69.8 - 801 °F |
||
| 15.1 µm/m-°C @Temperature 21.0 - 538 °C |
8.39 µin/in-°F @Temperature 69.8 - 1000 °F |
||
| 15.7 µm/m-°C @Temperature 21.1 - 649 °C |
8.72 µin/in-°F @Temperature 70.0 - 1200 °F |
||
| 16.5 µm/m-°C @Temperature 21.1 - 816 °C |
9.17 µin/in-°F @Temperature 70.0 - 1500 °F |
||
| 16.6 µm/m-°C @Temperature 21.1 - 871 °C |
9.22 µin/in-°F @Temperature 70.0 - 1600 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | 0.50 % | 0.50 % | |
| Chromium, Cr | 25.5 % | 25.5 % | |
| Cobalt, Co | 50 % | 50 % | As remainder |
| Iron, Fe | <= 2.0 % | <= 2.0 % | |
| Manganese, Mn | <= 1.0 % | <= 1.0 % | |
| Nickel, Ni | 10.5 % | 10.5 % | |
| Other | <= 2.0 % | <= 2.0 % | |
| Phosphorous, P | <= 0.040 % | <= 0.040 % | |
| Silicon, Si | <= 1.0 % | <= 1.0 % | |
| Sulfur, S | <= 0.040 % | <= 0.040 % | |
| Tungsten, W | 7.5 % | 7.5 % |
Users viewing this material also viewed the following:
- SABIC PVC 59S Suspension Polyvinyl Chloride for Rigid Products
- A. Schulman SCHULAMID® 66 GF33HS 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66
- Tipco Tipcolite® TG 613 Phenolic Compound, Mineral & Wood Flour, Soft Flow & Good Surface Finish
- Zig Sheng Industrial ZISAMIDE® TP4208 Nylon 6
- Formosa Plastics Formolene® 4100T Injection Molding Polypropylene
- Fainplast Compounds GA 72 Flexible PVC, Flame Retardant Sheathing
- Axiall 375 Wire & Cable Flexible PVC
- DSM Arnite® A04 900 PET (European Grade)
Copyright © lookpolymers.com All Rights Reserved